METHOD OF HARDENING CUTTING PART OF WORKING TOOLS

FIELD: technological processes.SUBSTANCE: invention relates to thermal hardening of high carbon alloys by using arc discharge plasma between part and tungsten electrode and can be used in production of working tools for soil development. To obtain a stable depth of ledeburite layer equal to 0.9-1.1 mm, increasing wear resistance of working tools of tillage tools made of high-strength cast iron VCh50, hardening of the cutting part of the working member is performed using arc reverse polarity plasma between the electrode and the hardened surface, the electrode used is a tungsten electrode, which performs axial longitudinal oscillations with frequency of 4-8 Hz and moves along hardened surface at rate of 0.4-1.5 cm/s, wherein time of each contact of tungsten electrode with hardened surface is 0.06-0.07 s.EFFECT: increased wear resistance of tillage working tools.1 cl, 2 ex Изобретение относится к области термического упрочнения высокоуглеродистых сплавов путем использования плазмы дугового разряда между деталью и вольфрамовым электродом и может быть использовано при производстве рабочих органов орудий для разработки грунтов. Для получения стабильной глубины ледебуритного слоя, равной 0,9-1,1 мм, повышения износостойкости лезвий рабочих органов почвообрабатывающих орудий из высокопрочного чугуна ВЧ50 осуществляют упрочнение режущей части рабочего органа с использованием плазмы дугового разряда обратной полярности между электродом и упрочняемой поверхностью, в качестве электрода используют вольфрамовый электрод, который осуществляет осевые продольные колебания с частотой 4-8 Гц и перемещается по упрочняемой поверхности со скоростью 0,4-1,5 см/с, при этом время каждого контакта вольфрамового электрода с упрочняемой поверхностью составляет 0,06-0,07 с. 2 пр.