HIGH-STRENGTH FOUNDRY ALUMINUM ALLOY WITH CALCIUM ADDITIVE

FIELD: metallurgy.SUBSTANCE: invention relates to metallurgy of aluminum-based materials and can be used in production of articles operating under high loads at temperatures of up to 150-200 °C, in particular, parts of aircrafts, cars and other vehicles, sports equipment parts, etc. Aluminium-based alloy contains following, wt%: 6.0-6.5 Zn, 1.0-1.5 Ca, 1.5-2.0 Mg, 0.5-0.8 Fe, the rest is aluminum. In particular cases during casting in graphite and steel mold the following level of mechanical properties is achieved without application of heat treatment: temporary resistance (σ) is not less than 330 MPa, yield point (σ) is not less than 220 MPa, relative elongation (δ) is not less than 4 %.EFFECT: invention is aimed at creation of foundry high-strength aluminum alloy intended for production of shaped castings.1 cl, 2 ex, 2 tbl, 4 dwg Изобретение относится к области металлургии материалов на основе алюминия и может быть использовано при получении изделий, работающих под действием высоких нагрузок при температурах до 150-200°С, в частности деталей летательных аппаратов, автомобилей и других транспортных средств, деталей спортинвентаря и др. Сплав на основе алюминия содержит, мас.%: 6,0-6,5 Zn, 1,0-1,5 Са, 1,5-2,0 Mg, 0,5-0,8 Fe, остальное - алюминий. Изобретение направлено на создание литейного высокопрочного алюминиевого сплава, предназначенного для получения фасонных отливок. В частных случаях при литье в графитовую и стальную изложницу достигается следующий уровень механических свойств без применения термической обработки: временное сопротивление (σ) - не менее 330 МПа, предел текучести (σ) - не менее 220 МПа, относительное удлинение (δ) - не менее 4%. 1 з.п. ф-лы, 2 пр., 2 табл., 4 ил.