DUPLEX STAINLESS STEEL FOR PRODUCTION OF SHUTOFF AND CONTROL VALVES

FIELD: metallurgy.SUBSTANCE: invention relates to duplex stainless steel used for production of shutoff and control valves of corrosion-active gas media with high content of hydrogen sulphide. Steel contains components at the following ratio, wt. %: carbon 0.01-0.04, silicon 0.3-0.5, manganese 0.9-1.2, chromium 22.5-24.0, nickel 5.8 -7.0, molybdenum 3.5-4.8, nitrogen 0.16-0.25, copper 3.0-3.3, niobium 0.27-0.37, cerium and/or lanthanum 0.001-0.004, sulfur ≤0.004, phosphorus ≤0.004, aluminum 0.01-0.02, calcium 0.001-0.004, yttrium ≤0.005, iron is the rest. After electroslag remelting, it has structure containing 50-60 vol. % of ferrite, inside which ferritic grains of which there are nitrides and nitrite carbonitrides of size ≤300 nm.EFFECT: higher visco-plastic characteristics of steel in combination with high corrosion resistance and resistance to corrosion cracking in aggressive gas mediums of hydrogen sulphide.1 cl, 2 tbl, 2 dwg Изобретение относится к области металлургии, а именно к дуплексной нержавеющей стали, используемой для производства запорной и регулирующей арматуры коррозионно-активных газовых сред с высоким содержанием сероводорода. Сталь содержит компоненты при следующем соотношении, мас.%: углерод 0,01-0,04, кремний 0,3-0,5, марганец 0,9-1,2, хром 22,5-24,0, никель 5,8-7,0, молибден 3,5-4,8, азот 0,16-0,25, медь 3,0-3,3, ниобий 0,27-0,37, церий и/или лантан 0,001-0,004, сера ≤0,004, фосфор ≤0,004, алюминий 0,01-0,02, кальций 0,001-0,004, иттрий ≤0,005, железо - остальное. После электрошлакового переплава она имеет структуру, содержащую 50-60 об.% феррита, внутри ферритных зерен которого расположены нитриды и карбонитриды ниобия размером ≤300 нм. Обеспечивается повышение вязко-пластических характеристик стали в сочетании с повышенной коррозионной стойкостью и стойкостью к коррозионному растрескиванию в агрессивных газовых средах сероводорода. 2 табл., 2 ил.