METHOD OF OBTAINING SILUMIN

FIELD: metallurgy.SUBSTANCE: invention relates to the metallurgy of non-ferrous metals, namely to the production of silumin using amorphous silica fume as a source of silicon. Method of obtaining silumin includes the introduction of silicon-containing oxide raw materials in the aluminum melt, mixing the melt and casting the resulting alloy, moreover, amorphous silica fume is used as a silicon-containing oxide raw material, which prior to its introduction into the melt is subjected to heat treatment at a temperature of 200-300 °C, the introduction of amorphous microsilica is carried out in a stream of inert gas with stirring, ensuring that the silica fume particles are drawn into the vortex funnel formed in liquid aluminum, and after mixing the melt is alloyed with magnesium in an amount up to 1 % wt.EFFECT: method allows efficiently and with minimal cost to obtain alloys that meet the requirements of GOST 1583-93 93 in chemical composition and mechanical properties.4 cl, 5 ex, 1 tbl, 3 dwg Изобретение относится к металлургии цветных металлов, а именно к получению силуминов с использованием в качестве источника кремния аморфного микрокремнезема. Способ получения силуминов включает введение кремнийсодержащего оксидного сырья в алюминиевый расплав, перемешивание расплава и разливку полученного сплава, причем в качестве кремнийсодержащего оксидного сырья используют аморфный микрокремнезем, который перед введением в расплав подвергают термической обработке при температуре 200-300°С, введение аморфного микрокремнезема осуществляют в потоке инертного газа с перемешиванием, обеспечивающим втягивание частиц микрокремнезема в вихревую воронку, образованную в жидком алюминии, а после перемешивания расплав легируют магнием в количестве до 1% масс. Способ позволяет эффективно и с минимальными затратами получать сплавы, соответствующие требованиям ГОСТ 1583-93 93 по химическому составу и механическим свойствам. 3 з.п. ф-лы, 5 пр., 1 табл., 3 ил.