METHOD FOR PRODUCING MOLDED CERAMIC MEMBRANE

FIELD: technological processes.SUBSTANCE: invention relates to production of molded ceramic membrane to be used in chemical, food, pharmaceutical and other industries. According to the method, rice husks are annealed at temperature of 300-400 °C in air, milled and fraction sized 0.1-0.2 mm is taken. Obtained powder is formed by pressing in vacuum chamber at 20.7-24.5 MPa to be consolidated under conditions of spark plasma sintering at temperature not lower than 1,800 °C.EFFECT: invention enables to obtain a membrane containing silicon carbide, which gives the membrane increased indices hardness, strength, electrical conductivity and specific surface.1 cl, 2 dwg, 3 tbl, 3 ex Изобретение относится к технологии получения формованной керамической мембраны, которая может быть использована в химической, пищевой, фармацевтической и других отраслях промышленности. Согласно способу рисовую шелуху обжигают при температуре 300-400°С на воздухе, измельчают, отбирают фракцию с размером частиц 0,1-0,2 мм. Полученный порошок подвергают формованию прессованием в вакуумной камере при давлении 20,7-24,5 МПа, осуществляя его консолидацию в условиях искрового плазменного спекания при температуре не ниже 1800°С. Изобретение обеспечивает получение мембраны, содержащей карбид кремния, придающий мембране повышенные показатели твердости, прочности, электропроводности, удельной поверхности. 1 з.п. ф-лы, 2 ил., 3 табл., 3 пр.