METHOD OF PROCESSING OF LIQUID-MOLTEN BLAST-FURNACE SLAG

FIELD: metallurgy.SUBSTANCE: invention relates to ferrous metallurgy and can be used in processing of liquid-molten blast-furnace slags. Liquid-molten blast-furnace slag is poured into trenches in layers, cooling a slag massif, dredging the slag massif, stacking and re-shoveling. At the same time, the slag is drained on a bed of cold blast-furnace slag until it forms an array of 0.3-1.5 m thick. Cooling is carried out in air for at least 10 hours, and re-shoveling - for at least 10 hours to a temperature of the slag array of not more than 100 °C. In addition, slag discharge is carried out on a bedding from a cold blast-furnace slag fraction from 0 to 700 mm and thickness of not more than 0.8 m.EFFECT: invention provides higher environmental purity of processing of liquid-molten blast-furnace slag by reducing gas emissions.3 cl Изобретение относится к черной металлургии и может быть использовано при переработке огненно-жидких доменных шлаков. Огненно-жидкий доменный шлак послойно сливают в траншею, осуществляют охлаждение массива шлака, выемку шлакового массива, укладку в штабель и перелопачивание. При этом слив шлака осуществляют на подсыпку из холодного доменного шлака до образования им массива толщиной 0,3-1,5 м. Охлаждение осуществляют на воздухе в течение не менее 10 часов, и перелопачивание - в течение не менее 10 часов до температуры шлакового массива не более 100°С. Кроме того, слив шлака осуществляют на подсыпку из холодного доменного шлака фракции от 0 до 700 мм и толщиной не более 0,8 м. Изобретение обеспечивает повышение экологической чистоты процесса переработки огненно-жидкого доменного шлака за счет снижения газовых выбросов. 2 з.п. ф-лы.