MICRO-ALLOYED HIGH-STRENGTH MULTI-PHASE STEEL CONTAINING SILICON WITH MINIMUM TENSILE STRENGTH OF 750 MPA IMPROVED PROPERTIES AND METHOD FOR PRODUCING A STRIP FROM SAID STEEL

FIELD: metallurgy.SUBSTANCE: invention relates to metallurgy, namely to a high-strength multi-phase steel meant for producing a cold- or hot-rolled strip used to manufacture a lightweight vehicle construction. Steel consists of the following elements, wt.%: C from ≥ 0.075 to ≤ 0.105; Si from ≥ 0.600 to ≤ 0.800; Mn from ≥ 1.000 to ≤ 1.900; Cr from ≥ 0.100 to ≤ 0.700; Al from ≥ 0.010 to ≤ 0.060; N from ≥ 0.0020 to ≤ 0.0120; S ≤ 0.0030; Nb from ≥ 0.005 to ≤ 0.050; Ti from ≥ 0.005 to ≤ 0.050; B from ≥ 0.0005 to ≤ 0.0040; Mo ≤ 0.200; Cu ≤ 0.040; Ni ≤ 0.040; rest - iron and contamination resulting from smelting.EFFECT: minimum tensile strength of 750 MPa, yield strength to strength ratios of up to 73 % and improved deformation properties are provided.42 cl, 6 dwg, 8 ex Изобретение относится к области металлургии, а именно к высокопрочной многофазной стали, предназначенной для получения холоднокатаной или горячекатаной ленты, используемой для изготовления облегченной конструкции автомобиля. Сталь содержит следующие элементы, мас.%: С от ≥ 0,075 до ≤ 0,105, Si от ≥ 0,600 до ≤ 0,800, Mn от ≥ 1,000 до ≤ 1,900, Cr от ≥ 0,100 до ≤ 0,700, Al от ≥ 0,010 до ≤ 0,060, N от ≥ 0,0020 до ≤ 0,0120, S ≤ 0,0030, Nb от ≥ 0,005 до ≤ 0,050, Ti от ≥ 0,005 до ≤ 0,050, B от ≥ 0,0005 до ≤ 0,0040, Mo ≤ 0,200, Cu ≤ 0,040, Ni ≤ 0,040, остальное - железо и обусловленные выплавкой примеси. Обеспечивается минимальный предел прочности на растяжение 750 МПа, отношение предела текучести к пределу прочности не более 73% и улучшенные деформационные свойства. 4 н. и 38 з.п. ф-лы, 6 ил., 8 пр.