MOULDING MIXTURE FOR PRODUCING CASTING MOULD WHEN CASTING MAGNESIUM ALLOYS

FIELD: metallurgy.SUBSTANCE: moulding mixture contains quartz sand, a binder and a non-stick additive in the form of silicon carbide in an amount of 4% to 36% by weight with respect to the total weight of the moulding mixture. Silicon carbide is a powder or micropowder with an average particle size of less than the average particle size of the sand used in the moulding mixture. The moulding mixture may further comprise oleophilic bentonite in the form of a dry powder or in a swollen state in an amount of 0.5% to 12% by weight with respect to the total weight of the moulding mixture.EFFECT: increase reliability of magnesium alloys protection against oxidation, cleanliness of castings surface.3 cl, 2 tbl Изобретение относится к литейному производству и предназначено для песчано-смоляных и песчано-глинистых форм, используемых при литье магниевых сплавов. Формовочная смесь содержит кварцевый песок, связующее и противопригарную добавку в виде карбида кремния в количестве от 4% до 36 мас.% по отношению к общей массе формовочной смеси. Карбид кремния представляет собой порошок или микропорошок со средним размером частиц менее среднего размера частиц песка, используемого в формовочной смеси. Формовочная смесь дополнительно может содержать олеофильный бентонит в виде сухого порошка или в набухшем состоянии в количестве от 0,5% до 12 мас.% по отношению к общей массе формовочной смеси. Обеспечивается повышение надежности защиты магниевых сплавов от окисления, чистоты поверхности отливок. 2 з.п. ф-лы, 2 табл.