POLYMER COMPOSITION

FIELD: chemistry.SUBSTANCE: rubber mixture contains the components at the following ratio, wt %: synthetic isoprene rubber 18.7-24.021; synthetic butadiene rubber 6.005-7.547; synthetic rubber butadiene styrene 18.02-18.87; zinc oxide 1.802-1.887; sulfur technical 0.601-0.943; sulfenamide C 0.300-1.132; stearic acid 1.201-1.132; technical carbon P234 6.005-7.547; technical carbon P514 22.64-24.02; glass of ground fraction 50-100 microns 5.660-6.005; a mixture of fullerenes of fraction C-C0.001-0.015; acetononyl H 1.132-1.201; wax VIZ 1.802-1.887; oil for oil PN 3.003-3.019; bitumen petroleum alkaline 6.005-7.547.EFFECT: invention allows to manufacture specialty rubber products with high frictional resistance, with improved physical and mechanical characteristics and the ability to work in aggressive environments.2 tbl, 3 ex Изобретение относится к химической промышленности, в частности к производству резиновых смесей, и может быть использовано в производстве резинотехнических изделий. Резиновая смесь содержит компоненты при следующем соотношении, мас. %: синтетический изопреновый каучук 18,7-24,021; синтетический каучук бутадиеновый 6,005-7,547; синтетический каучук бутадиенстирольный 18,02-18,87; окись цинка 1,802-1,887; серу техническую 0,601-0,943; сульфенамид Ц 0,300-1,132; кислоту стеариновую 1,201-1,132; углерод технический П234 6,005-7,547; углерод технический П514 22,64-24,02; стекло молотое фракции 50-100 мкм 5,660-6,005; смесь фуллеренов фракции С-С0,001-0,015; ацетонанил Н 1,132-1,201; воск ЗВП 1,802-1,887; масло нефтяное ПН6 3,003-3,019; битум нефтяной щелочной 6,005-7,547. Изобретение позволяет изготавливать резинотехнические изделия специального назначения, обладающие высоким сопротивлением трению, с улучшенными физико-механическими характеристиками и возможностью работы в агрессивных средах. 2 табл., 3 пр.