PRODUCTION METHOD OF REINFORCED NANOCOMPOSIT MATERIAL BASED ON MAGNESIUM

FIELD: metallurgy.SUBSTANCE: addition alloy is prepared in the form of compact rods from the uniformly agitated mixture of magnesium powder and aluminium nitride nanopowder with the particles diameter in the range of 30÷80 nm. The produced rods are introduced into the melt of the matrix based on magnesium to provide the aluminium nitride nanopowder content in the resulting nanocomposite material 1±0.2 wt % and are held at the matrix melt temperature of at least 35 minutes, while simultaneous exposing to the melt by ultrasound with the intensity of 20÷25 W/cmand the oscillation frequency 17÷19 kHz.EFFECT: ultimate tensile strength increase more than in two times with simultaneous increase of the resulted material ductility.1 ex Изобретение относится к получению упрочненного нанокомпозиционного материала, который может быть использован в авиастроении и в автомобильной промышленности. Готовят лигатуру в виде компактированных стержней из равномерно перемешанной смеси порошка магния и нанопорошка нитрида алюминия с диаметром частиц в диапазоне 30÷80 нм. Полученные стержни вводят в расплав матрицы на основе магния с обеспечением содержания нанопорошка нитрида алюминия в получаемом нанокомпозиционном материале 1±0,2 мас.% и выдерживают при температуре расплава матрицы в течение не менее 35 мин при одновременном воздействии на расплав ультразвуком интенсивностью 20÷25 Вт/сми частотой колебаний 17÷19 кГц. Обеспечивается увеличение предела прочности при растяжении более чем в два раза с одновременным увеличением пластичности полученного материала. 1 пр.