GALVANIZED STEEL SHEET AND METHOD OF PRODUCTION THEREOF

FIELD: metallurgy.SUBSTANCE: galvanized steel sheet has a specific weight from 5.5 to 7.5, and comprises a steel sheet and a zinc layer coated on its surface. The steel sheet has the following composition, wt %: from more than 0.100 to 0.500 C, from 0.0001 to less than 0.20 Si, from more than 0.20 to 3.00 Mn, 3.0-10.0 Al, 0.0030-0.0100 N, from more than 0.100 to 1.000 Ti, 0.00001-0.0200 P, 0.00001-0.0100 S, Fe and unavoidable impurities - the rest. Zinc layer has the following composition, wt %: 0.01-15 Fe, 0.05-1.0 Ni, 0.15-2.0 Al, Zn and unavoidable impurities - the rest.EFFECT: produced sheets have a low specific weight, high galvanising properties and suitability for hole expansion.8 cl, 1 dwg, 6 tbl, 4 ex Изобретение относится к области металлургии, а именно к получению оцинкованного стального листа, используемого в автомобилестроении. Оцинкованный стальной лист имеет удельный вес от 5,5 до 7,5 и включает стальной лист и нанесенный на его поверхность цинковый слой. Стальной лист имеет следующий состав, в мас.%: от более 0,100 до 0,500 С, от 0,0001 до менее 0,20 Si, от более 0,20 до 3,00 Mn, 3,0-10,0 Al, 0,0030-0,0100 N, от более 0,100 до 1,000 Ti, 0,00001-0,0200 Р, 0,00001-0,0100 S, Fe и неизбежные примеси - остальное. Цинковый слой имеет следующий состав, в мас.%: 0,01-15 Fe, 0,05-1,0 Ni, 0,15-2,0 Al, Zn и неизбежные примеси - остальное. Изготавливаемые листы обладают низким удельным весом, высокими характеристиками цинкования и пригодностью к расширению отверстия. 2 н. и 6 з.п. ф-лы, 1 ил., 6 табл., 4 пр.