METHOD OF MANUFACTURING SELF-HEATED HOLLOW CATHODE FROM TITANIUM NITRIDE FOR PLASMA GENERATION SYSTEMS

FIELD: electricity.SUBSTANCE: method of manufacturing a self-heated hollow cathode from titanium nitride for plasma generation systems includes forming a tubular article from the mixture of powders containing titanium nitride, 10% by weight of titanium, not more than 2% by weight of polyvinyl butyral plasticiser, by pulsed or static pressing, extrusion, slip casting or by an alternative method, annealing the tubular article in a vacuum oven in the nitrogen stream at the pressure of 1 Pa at the temperature of 500°C for 1 hour for thermal decomposition of the plasticiser and removal of the decomposition products from the tubular article volume, mounting the tubular article as a cathode electrode into the electric discharge system containing an anode electrode, continuously pumping nitrogen through the tubular article, applying voltage between the anode and the tubular article and the ignition of the glow discharge between the tubular article and the anode, the current of which is gradually increased in the process of the arcing ceasing, which ensures the removal of surface contamination and the temperature rise of the tubular article, the discharge transition to the thermionic arc mode and heating the cathode to the temperature of 2000°C.EFFECT: holding the formed tubular article in the plasma of its own discharge as a cathode electrode, while operating in the thermionic arc mode, provides its solid-phase sintering and forming a self-adhesive hollow cathode made of titanium nitride with the high density, the thermoemission properties and the increased service life.3 dwg Изобретение относится к плазменной технике и может быть использовано в газоразрядных устройствах с самонакаливаемым полым катодом. Способ изготовления самонакаливаемого полого катода из нитрида титана для систем генерации плазмы включает формирование трубчатого изделия из смеси порошков, содержащей нитрид титана, 10 вес.% титана, не более 2 вес.% пластификатора поливинилбутираля, импульсным или статическим прессованием, экструзией, шликерным литьем или альтернативным способом, отжиг трубчатого изделия в вакуумной печи в потоке азота при давлении 1 Па при температуре 500°С в течение 1 ч для термического разложения пластификатора и удаления продуктов разложения из объема трубчатого изделия, установку трубчатого изделия в качестве катодного электрода в электроразрядную систему, содержащую анодный электрод, постоянную прокачку азота через трубчатое изделие, приложение между анодом и трубчатым изд