METHOD OF APPLYING COATING OF ANTIFRICTION HARD ALLOY

FIELD: metallurgy.SUBSTANCE: powder material consisting of layers of titanium powder and a mixture of chromium and titanium carbide powders in a ratio of 78 wt % CrCand 22 wt % Ti is spread over the surface of the metal substrate, an intermediate layer of a mixture of chromium carbide and titanium carbide powders is placed between a layer of titanium powder and a layer of powder mixture in a ratio of 60 wt %CrCand 40 wt % Ti, the thickness of the latter is 0.8-1.2 times the thickness of the titanium powder layer. After that, an explosive charge is triggered. The explosive is located above the powder material separated from it by a metal plate. A normal incidence detonation wave compacts the powder material to a practically non-porous state and creates the conditions for connecting the components together and with the steel substrate.EFFECT: increased strength of the coating bond with the metal substrate.2 dwg, 3 tbl, 1 ex Изобретение относится к нанесению покрытия из антифрикционного твердого сплава на металлическую подложку. На поверхность металлической подложки размещают порошковый материал, состоящий из слоев титанового порошка и смеси порошков карбида хрома и титана в соотношении 78 мас. % CrCи 22 мас. % Ti, между слоем из титанового порошка и слоем из смеси порошков размещают промежуточный слой из смеси порошков карбида хрома и титана в соотношении 60 мас. % CrCи 40 мас. % Ti, при этом толщина последнего составляет 0,8-1,2 толщины слоя из титанового порошка. После инициируют заряд взрывчатого вещества, расположенный над порошковым материалом, отделенного от него металлической пластиной. Нормально падающая детонационная волна уплотняет порошковый материал до практически беспористого состояния и создает условия для соединения компонентов между собой и со стальной подложкой. Технический результат заключается в увеличении прочности соединения покрытия с металлической подложкой. 2 ил., 3 табл., 1 пр.