METHOD OF PRODUCING ROLLED STEEL SHEET FROM ALLOY OF Ti - 10,0-15,0 Al- 17,0-25,0 Nb - 2,0-4,0 V - 1,0-3,0 Mo - 0,1-1,0 Fe - 1,0-2,0 Zr - 0,3-0,6 Si

FIELD: metallurgy.SUBSTANCE: method of producing rolled steel sheet from alloy of Ti - 10,0-15,0 Al - 17,0-25,0 Nb - 2,0-4,0 V - 1,0-3,0 Mo - 0,1- 1,0 Fe - 1,0-2,0 Zr - 0,3-0,6 Si comprises forging of the ingot into a slab, mechanical treatment of the slab, multistage hot longitudinal rolling of the...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Hauptverfasser: Vodolazskij Valerij Fedorovich, Mikhajlov Vitalij Anatolevich, Leder Mikhail Ottovich, Vodolazskij Fedor Valerevich, Kozlov Aleksandr Nikolaevich, Kalienko Maksim Sergeevich
Format: Patent
Sprache:eng ; rus
Schlagworte:
Online-Zugang:Volltext bestellen
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
container_end_page
container_issue
container_start_page
container_title
container_volume
creator Vodolazskij Valerij Fedorovich
Mikhajlov Vitalij Anatolevich
Leder Mikhail Ottovich
Vodolazskij Fedor Valerevich
Kozlov Aleksandr Nikolaevich
Kalienko Maksim Sergeevich
description FIELD: metallurgy.SUBSTANCE: method of producing rolled steel sheet from alloy of Ti - 10,0-15,0 Al - 17,0-25,0 Nb - 2,0-4,0 V - 1,0-3,0 Mo - 0,1- 1,0 Fe - 1,0-2,0 Zr - 0,3-0,6 Si comprises forging of the ingot into a slab, mechanical treatment of the slab, multistage hot longitudinal rolling of the slab to semi-finished rolled stock, cutting of the semi-finished rolled stock into blanks, their adjustment processing, assembly into the package, the package rolling and the final adjustment processing of the sheets. Deformation of the ingot by forging into a slab is carried out in β-area at a temperature of Tpt+(120÷200)°C. In the first stage the rolling of the slab is carried out in β-area, in the penultimate stage in (α+β)-area, the final rolling to the semi-finished rolled stock is carried out in (α+β)-area. Assembly of the blanks into a package is carried out so that their rolling direction equals 90° angle relative to the rolling direction of the semi-finished rolled stock, pack rolling is carried out in (α+β)-area followed by quenching in water. Then, packet disassembly and cold rolling of each ingot with intermediate vacuum annealing are carried out.EFFECT: rolled steel sheet has high structural and technological properties.2 dwg, 2 tbl Изобретение относится к обработке металлов и сплавов давлением, а именно к способам изготовления тонколистового проката на основе алюминидов титана. Способ изготовления тонколистового проката из сплава Ti - 10,0-15,0 Al - 17,0-25,0 Nb - 2,0-4,0 V - 1,0-3,0 Mo - 0,1-1,0 Fe - 1,0-2,0 Zr - 0,3-0,6 Si включает ковку слитка в сляб, механическую обработку сляба, многоэтапную горячую продольную прокатку сляба на подкат, резку подката на листовые заготовки, их адъюстажную обработку, сборку в пакет, прокатку пакета и окончательную адъюстажную обработку листов. Деформацию слитка ковкой в сляб производят в β-области при температуре Тпп+(120÷200)°С. На первом этапе прокатку сляба в подкат осуществляют в β-области, на предпоследнем этапе в (α+β)-области, окончательную прокатку в подкат проводят в (α+β)-области. Осуществляют сборку листовых заготовок в пакет таким образом, что направление их прокатки составляет угол 90° относительно направления прокатки подката, пакетную прокатку осуществляют в (α+β)-области с последующей закалкой в воде. Затем осуществляют разборку пакета и холодную прокатку каждой заготовки с промежуточными вакуумными отжигами. Тонколистовой прокат обладает высокими конструкционными и технологическими свойствами, г
format Patent
fullrecord <record><control><sourceid>epo_EVB</sourceid><recordid>TN_cdi_epo_espacenet_RU2615761C1</recordid><sourceformat>XML</sourceformat><sourcesystem>PC</sourcesystem><sourcerecordid>RU2615761C1</sourcerecordid><originalsourceid>FETCH-epo_espacenet_RU2615761C13</originalsourceid><addsrcrecordid>eNqNikEOgjAQRdm4MOod5gBt0oLAmkArJoWaUkx0Q9DUhIQIEY_igR0MB3A1_817a-9TCJvrDLSEk9FZnR7LAxitlMigskIoqHIhLEijC0iU0pc5tR1Q4IwwykPCIOmRYiR_pvKG0kfaI5znEHeAuxgQGOEUHyDdYrCE6-tnAspIBFW39VaPtp_cbrkbD6SwaU7dODRuGtu7e7p3Y2o_4mEc8ZQHfyRfEYs6UQ</addsrcrecordid><sourcetype>Open Access Repository</sourcetype><iscdi>true</iscdi><recordtype>patent</recordtype></control><display><type>patent</type><title>METHOD OF PRODUCING ROLLED STEEL SHEET FROM ALLOY OF Ti - 10,0-15,0 Al- 17,0-25,0 Nb - 2,0-4,0 V - 1,0-3,0 Mo - 0,1-1,0 Fe - 1,0-2,0 Zr - 0,3-0,6 Si</title><source>esp@cenet</source><creator>Vodolazskij Valerij Fedorovich ; Mikhajlov Vitalij Anatolevich ; Leder Mikhail Ottovich ; Vodolazskij Fedor Valerevich ; Kozlov Aleksandr Nikolaevich ; Kalienko Maksim Sergeevich</creator><creatorcontrib>Vodolazskij Valerij Fedorovich ; Mikhajlov Vitalij Anatolevich ; Leder Mikhail Ottovich ; Vodolazskij Fedor Valerevich ; Kozlov Aleksandr Nikolaevich ; Kalienko Maksim Sergeevich</creatorcontrib><description>FIELD: metallurgy.SUBSTANCE: method of producing rolled steel sheet from alloy of Ti - 10,0-15,0 Al - 17,0-25,0 Nb - 2,0-4,0 V - 1,0-3,0 Mo - 0,1- 1,0 Fe - 1,0-2,0 Zr - 0,3-0,6 Si comprises forging of the ingot into a slab, mechanical treatment of the slab, multistage hot longitudinal rolling of the slab to semi-finished rolled stock, cutting of the semi-finished rolled stock into blanks, their adjustment processing, assembly into the package, the package rolling and the final adjustment processing of the sheets. Deformation of the ingot by forging into a slab is carried out in β-area at a temperature of Tpt+(120÷200)°C. In the first stage the rolling of the slab is carried out in β-area, in the penultimate stage in (α+β)-area, the final rolling to the semi-finished rolled stock is carried out in (α+β)-area. Assembly of the blanks into a package is carried out so that their rolling direction equals 90° angle relative to the rolling direction of the semi-finished rolled stock, pack rolling is carried out in (α+β)-area followed by quenching in water. Then, packet disassembly and cold rolling of each ingot with intermediate vacuum annealing are carried out.EFFECT: rolled steel sheet has high structural and technological properties.2 dwg, 2 tbl Изобретение относится к обработке металлов и сплавов давлением, а именно к способам изготовления тонколистового проката на основе алюминидов титана. Способ изготовления тонколистового проката из сплава Ti - 10,0-15,0 Al - 17,0-25,0 Nb - 2,0-4,0 V - 1,0-3,0 Mo - 0,1-1,0 Fe - 1,0-2,0 Zr - 0,3-0,6 Si включает ковку слитка в сляб, механическую обработку сляба, многоэтапную горячую продольную прокатку сляба на подкат, резку подката на листовые заготовки, их адъюстажную обработку, сборку в пакет, прокатку пакета и окончательную адъюстажную обработку листов. Деформацию слитка ковкой в сляб производят в β-области при температуре Тпп+(120÷200)°С. На первом этапе прокатку сляба в подкат осуществляют в β-области, на предпоследнем этапе в (α+β)-области, окончательную прокатку в подкат проводят в (α+β)-области. Осуществляют сборку листовых заготовок в пакет таким образом, что направление их прокатки составляет угол 90° относительно направления прокатки подката, пакетную прокатку осуществляют в (α+β)-области с последующей закалкой в воде. Затем осуществляют разборку пакета и холодную прокатку каждой заготовки с промежуточными вакуумными отжигами. Тонколистовой прокат обладает высокими конструкционными и технологическими свойствами, гарантирующими уровень временного сопротивления σ&gt;1000 МПа и относительного удлинения δ≥3,5%. 2 ил., 2 табл.</description><language>eng ; rus</language><subject>CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS ANDNON-FERROUS ALLOYS ; CHEMISTRY ; FERROUS OR NON-FERROUS ALLOYS ; MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVINGMATERIAL ; METALLURGY ; PERFORMING OPERATIONS ; PUNCHING METAL ; ROLLING OF METAL ; TRANSPORTING ; TREATMENT OF ALLOYS OR NON-FERROUS METALS</subject><creationdate>2017</creationdate><oa>free_for_read</oa><woscitedreferencessubscribed>false</woscitedreferencessubscribed></display><links><openurl>$$Topenurl_article</openurl><openurlfulltext>$$Topenurlfull_article</openurlfulltext><thumbnail>$$Tsyndetics_thumb_exl</thumbnail><linktohtml>$$Uhttps://worldwide.espacenet.com/publicationDetails/biblio?FT=D&amp;date=20170411&amp;DB=EPODOC&amp;CC=RU&amp;NR=2615761C1$$EHTML$$P50$$Gepo$$Hfree_for_read</linktohtml><link.rule.ids>230,308,780,885,25564,76547</link.rule.ids><linktorsrc>$$Uhttps://worldwide.espacenet.com/publicationDetails/biblio?FT=D&amp;date=20170411&amp;DB=EPODOC&amp;CC=RU&amp;NR=2615761C1$$EView_record_in_European_Patent_Office$$FView_record_in_$$GEuropean_Patent_Office$$Hfree_for_read</linktorsrc></links><search><creatorcontrib>Vodolazskij Valerij Fedorovich</creatorcontrib><creatorcontrib>Mikhajlov Vitalij Anatolevich</creatorcontrib><creatorcontrib>Leder Mikhail Ottovich</creatorcontrib><creatorcontrib>Vodolazskij Fedor Valerevich</creatorcontrib><creatorcontrib>Kozlov Aleksandr Nikolaevich</creatorcontrib><creatorcontrib>Kalienko Maksim Sergeevich</creatorcontrib><title>METHOD OF PRODUCING ROLLED STEEL SHEET FROM ALLOY OF Ti - 10,0-15,0 Al- 17,0-25,0 Nb - 2,0-4,0 V - 1,0-3,0 Mo - 0,1-1,0 Fe - 1,0-2,0 Zr - 0,3-0,6 Si</title><description>FIELD: metallurgy.SUBSTANCE: method of producing rolled steel sheet from alloy of Ti - 10,0-15,0 Al - 17,0-25,0 Nb - 2,0-4,0 V - 1,0-3,0 Mo - 0,1- 1,0 Fe - 1,0-2,0 Zr - 0,3-0,6 Si comprises forging of the ingot into a slab, mechanical treatment of the slab, multistage hot longitudinal rolling of the slab to semi-finished rolled stock, cutting of the semi-finished rolled stock into blanks, their adjustment processing, assembly into the package, the package rolling and the final adjustment processing of the sheets. Deformation of the ingot by forging into a slab is carried out in β-area at a temperature of Tpt+(120÷200)°C. In the first stage the rolling of the slab is carried out in β-area, in the penultimate stage in (α+β)-area, the final rolling to the semi-finished rolled stock is carried out in (α+β)-area. Assembly of the blanks into a package is carried out so that their rolling direction equals 90° angle relative to the rolling direction of the semi-finished rolled stock, pack rolling is carried out in (α+β)-area followed by quenching in water. Then, packet disassembly and cold rolling of each ingot with intermediate vacuum annealing are carried out.EFFECT: rolled steel sheet has high structural and technological properties.2 dwg, 2 tbl Изобретение относится к обработке металлов и сплавов давлением, а именно к способам изготовления тонколистового проката на основе алюминидов титана. Способ изготовления тонколистового проката из сплава Ti - 10,0-15,0 Al - 17,0-25,0 Nb - 2,0-4,0 V - 1,0-3,0 Mo - 0,1-1,0 Fe - 1,0-2,0 Zr - 0,3-0,6 Si включает ковку слитка в сляб, механическую обработку сляба, многоэтапную горячую продольную прокатку сляба на подкат, резку подката на листовые заготовки, их адъюстажную обработку, сборку в пакет, прокатку пакета и окончательную адъюстажную обработку листов. Деформацию слитка ковкой в сляб производят в β-области при температуре Тпп+(120÷200)°С. На первом этапе прокатку сляба в подкат осуществляют в β-области, на предпоследнем этапе в (α+β)-области, окончательную прокатку в подкат проводят в (α+β)-области. Осуществляют сборку листовых заготовок в пакет таким образом, что направление их прокатки составляет угол 90° относительно направления прокатки подката, пакетную прокатку осуществляют в (α+β)-области с последующей закалкой в воде. Затем осуществляют разборку пакета и холодную прокатку каждой заготовки с промежуточными вакуумными отжигами. Тонколистовой прокат обладает высокими конструкционными и технологическими свойствами, гарантирующими уровень временного сопротивления σ&gt;1000 МПа и относительного удлинения δ≥3,5%. 2 ил., 2 табл.</description><subject>CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS ANDNON-FERROUS ALLOYS</subject><subject>CHEMISTRY</subject><subject>FERROUS OR NON-FERROUS ALLOYS</subject><subject>MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVINGMATERIAL</subject><subject>METALLURGY</subject><subject>PERFORMING OPERATIONS</subject><subject>PUNCHING METAL</subject><subject>ROLLING OF METAL</subject><subject>TRANSPORTING</subject><subject>TREATMENT OF ALLOYS OR NON-FERROUS METALS</subject><fulltext>true</fulltext><rsrctype>patent</rsrctype><creationdate>2017</creationdate><recordtype>patent</recordtype><sourceid>EVB</sourceid><recordid>eNqNikEOgjAQRdm4MOod5gBt0oLAmkArJoWaUkx0Q9DUhIQIEY_igR0MB3A1_817a-9TCJvrDLSEk9FZnR7LAxitlMigskIoqHIhLEijC0iU0pc5tR1Q4IwwykPCIOmRYiR_pvKG0kfaI5znEHeAuxgQGOEUHyDdYrCE6-tnAspIBFW39VaPtp_cbrkbD6SwaU7dODRuGtu7e7p3Y2o_4mEc8ZQHfyRfEYs6UQ</recordid><startdate>20170411</startdate><enddate>20170411</enddate><creator>Vodolazskij Valerij Fedorovich</creator><creator>Mikhajlov Vitalij Anatolevich</creator><creator>Leder Mikhail Ottovich</creator><creator>Vodolazskij Fedor Valerevich</creator><creator>Kozlov Aleksandr Nikolaevich</creator><creator>Kalienko Maksim Sergeevich</creator><scope>EVB</scope></search><sort><creationdate>20170411</creationdate><title>METHOD OF PRODUCING ROLLED STEEL SHEET FROM ALLOY OF Ti - 10,0-15,0 Al- 17,0-25,0 Nb - 2,0-4,0 V - 1,0-3,0 Mo - 0,1-1,0 Fe - 1,0-2,0 Zr - 0,3-0,6 Si</title><author>Vodolazskij Valerij Fedorovich ; Mikhajlov Vitalij Anatolevich ; Leder Mikhail Ottovich ; Vodolazskij Fedor Valerevich ; Kozlov Aleksandr Nikolaevich ; Kalienko Maksim Sergeevich</author></sort><facets><frbrtype>5</frbrtype><frbrgroupid>cdi_FETCH-epo_espacenet_RU2615761C13</frbrgroupid><rsrctype>patents</rsrctype><prefilter>patents</prefilter><language>eng ; rus</language><creationdate>2017</creationdate><topic>CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS ANDNON-FERROUS ALLOYS</topic><topic>CHEMISTRY</topic><topic>FERROUS OR NON-FERROUS ALLOYS</topic><topic>MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVINGMATERIAL</topic><topic>METALLURGY</topic><topic>PERFORMING OPERATIONS</topic><topic>PUNCHING METAL</topic><topic>ROLLING OF METAL</topic><topic>TRANSPORTING</topic><topic>TREATMENT OF ALLOYS OR NON-FERROUS METALS</topic><toplevel>online_resources</toplevel><creatorcontrib>Vodolazskij Valerij Fedorovich</creatorcontrib><creatorcontrib>Mikhajlov Vitalij Anatolevich</creatorcontrib><creatorcontrib>Leder Mikhail Ottovich</creatorcontrib><creatorcontrib>Vodolazskij Fedor Valerevich</creatorcontrib><creatorcontrib>Kozlov Aleksandr Nikolaevich</creatorcontrib><creatorcontrib>Kalienko Maksim Sergeevich</creatorcontrib><collection>esp@cenet</collection></facets><delivery><delcategory>Remote Search Resource</delcategory><fulltext>fulltext_linktorsrc</fulltext></delivery><addata><au>Vodolazskij Valerij Fedorovich</au><au>Mikhajlov Vitalij Anatolevich</au><au>Leder Mikhail Ottovich</au><au>Vodolazskij Fedor Valerevich</au><au>Kozlov Aleksandr Nikolaevich</au><au>Kalienko Maksim Sergeevich</au><format>patent</format><genre>patent</genre><ristype>GEN</ristype><title>METHOD OF PRODUCING ROLLED STEEL SHEET FROM ALLOY OF Ti - 10,0-15,0 Al- 17,0-25,0 Nb - 2,0-4,0 V - 1,0-3,0 Mo - 0,1-1,0 Fe - 1,0-2,0 Zr - 0,3-0,6 Si</title><date>2017-04-11</date><risdate>2017</risdate><abstract>FIELD: metallurgy.SUBSTANCE: method of producing rolled steel sheet from alloy of Ti - 10,0-15,0 Al - 17,0-25,0 Nb - 2,0-4,0 V - 1,0-3,0 Mo - 0,1- 1,0 Fe - 1,0-2,0 Zr - 0,3-0,6 Si comprises forging of the ingot into a slab, mechanical treatment of the slab, multistage hot longitudinal rolling of the slab to semi-finished rolled stock, cutting of the semi-finished rolled stock into blanks, their adjustment processing, assembly into the package, the package rolling and the final adjustment processing of the sheets. Deformation of the ingot by forging into a slab is carried out in β-area at a temperature of Tpt+(120÷200)°C. In the first stage the rolling of the slab is carried out in β-area, in the penultimate stage in (α+β)-area, the final rolling to the semi-finished rolled stock is carried out in (α+β)-area. Assembly of the blanks into a package is carried out so that their rolling direction equals 90° angle relative to the rolling direction of the semi-finished rolled stock, pack rolling is carried out in (α+β)-area followed by quenching in water. Then, packet disassembly and cold rolling of each ingot with intermediate vacuum annealing are carried out.EFFECT: rolled steel sheet has high structural and technological properties.2 dwg, 2 tbl Изобретение относится к обработке металлов и сплавов давлением, а именно к способам изготовления тонколистового проката на основе алюминидов титана. Способ изготовления тонколистового проката из сплава Ti - 10,0-15,0 Al - 17,0-25,0 Nb - 2,0-4,0 V - 1,0-3,0 Mo - 0,1-1,0 Fe - 1,0-2,0 Zr - 0,3-0,6 Si включает ковку слитка в сляб, механическую обработку сляба, многоэтапную горячую продольную прокатку сляба на подкат, резку подката на листовые заготовки, их адъюстажную обработку, сборку в пакет, прокатку пакета и окончательную адъюстажную обработку листов. Деформацию слитка ковкой в сляб производят в β-области при температуре Тпп+(120÷200)°С. На первом этапе прокатку сляба в подкат осуществляют в β-области, на предпоследнем этапе в (α+β)-области, окончательную прокатку в подкат проводят в (α+β)-области. Осуществляют сборку листовых заготовок в пакет таким образом, что направление их прокатки составляет угол 90° относительно направления прокатки подката, пакетную прокатку осуществляют в (α+β)-области с последующей закалкой в воде. Затем осуществляют разборку пакета и холодную прокатку каждой заготовки с промежуточными вакуумными отжигами. Тонколистовой прокат обладает высокими конструкционными и технологическими свойствами, гарантирующими уровень временного сопротивления σ&gt;1000 МПа и относительного удлинения δ≥3,5%. 2 ил., 2 табл.</abstract><oa>free_for_read</oa></addata></record>
fulltext fulltext_linktorsrc
identifier
ispartof
issn
language eng ; rus
recordid cdi_epo_espacenet_RU2615761C1
source esp@cenet
subjects CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS ANDNON-FERROUS ALLOYS
CHEMISTRY
FERROUS OR NON-FERROUS ALLOYS
MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVINGMATERIAL
METALLURGY
PERFORMING OPERATIONS
PUNCHING METAL
ROLLING OF METAL
TRANSPORTING
TREATMENT OF ALLOYS OR NON-FERROUS METALS
title METHOD OF PRODUCING ROLLED STEEL SHEET FROM ALLOY OF Ti - 10,0-15,0 Al- 17,0-25,0 Nb - 2,0-4,0 V - 1,0-3,0 Mo - 0,1-1,0 Fe - 1,0-2,0 Zr - 0,3-0,6 Si
url https://sfx.bib-bvb.de/sfx_tum?ctx_ver=Z39.88-2004&ctx_enc=info:ofi/enc:UTF-8&ctx_tim=2025-01-06T13%3A49%3A02IST&url_ver=Z39.88-2004&url_ctx_fmt=infofi/fmt:kev:mtx:ctx&rfr_id=info:sid/primo.exlibrisgroup.com:primo3-Article-epo_EVB&rft_val_fmt=info:ofi/fmt:kev:mtx:patent&rft.genre=patent&rft.au=Vodolazskij%20Valerij%20Fedorovich&rft.date=2017-04-11&rft_id=info:doi/&rft_dat=%3Cepo_EVB%3ERU2615761C1%3C/epo_EVB%3E%3Curl%3E%3C/url%3E&disable_directlink=true&sfx.directlink=off&sfx.report_link=0&rft_id=info:oai/&rft_id=info:pmid/&rfr_iscdi=true