IMPROVED METHOD OF GAS-PHASE POLYMERIZATION, INCLUDING POLYMER LAYER HIGH VOLUMETRIC DENSITY

FIELD: technological processes.SUBSTANCE: invention relates to improved method of gas-phase olefin polymerization, having relatively high polymer layer apparent density. Described is propylene polymerization method in direct flow gas-core reactor in presence of catalyst composition and mixed external electron-donating system. First external electrons donor is carboxylate compound. Gas-core reactor contains polymer layer with fluidization layer volumetric density of 128 kg/m. Reduced gas flow rate in gas-core reactor is in 10 times less than minimum fluidization rate. Volume fraction of solid substance in gas-solid substance system exceeds value of 0.17.EFFECT: preventing local overheating in reactor, which can be related to polymer particles agglomeration or formation of lumps, due to application of new external electron-donating system.14 cl, 1 tbl, 4 ex Изобретение относится к улучшению способа газофазной олефиновой полимеризации, имеющего относительно высокую объемную плотность полимерного слоя. Описан способ полимеризации пропилена в прямоточном газофазном реакторе в присутствии каталитической композиции и смешанной внешней электронодонорной системы. Первый внешний донор электронов представляет собой карбоксилатное соединение. Газофазный реактор содержит полимерный слой с объемной плотностью псевдоожиженого слоя больше 128 кг/м. Приведенная скорость потока газа в газофазном реакторе в 10 раз меньше, чем минимальная скорость псевдоожижения. Объемная доля твердого вещества в системе газ-твердое вещество превышает величину 0,17. Технический результат - предотвращение локального перегрева в реакторе, который может быть связан с агломерацией частиц полимера или образованием комков, за счет применения новой внешней электронодонорной системы. 13 з.п. ф-лы, 1 табл., 4 пр.