LOW ALLOYED STEEL FOR OILFIELD GAGE PIPES HAVING EXCELLENT RESISTANCE TO SULPHIDE STRESS CRACKING, AND ITS MANUFACTURING METHOD

FIELD: metallurgy.SUBSTANCE: invention relates to metallurgy, namely to low-alloy steel for oilfield gage pipes. Steel has chemical composition, containing, in wt%: C: from 0.56 to 1.00, Si: from 0.05 to 0.50, Mn: from 0.05 to 1.00, P: not exceeding 0.025, S: not exceeding 0.010, Al: from 0.005 to 0.100, Mo: from 0.40 to 1.00, V: from 0.07 to 0.30, O: not exceeding 0.010, N: not exceeding 0.03, rest is Fe and unavoidable impurities. Steel has yield point, making at least 862 MPa, and diffraction maximum width at half height for crystal lattice plane [211], obtained by x-ray diffraction measurement is not more than 0.50°.EFFECT: steel has high mechanical properties and resistance to corrosion in sulphide containing environment.22 cl, 4 dwg, 4 tbl, 2 ex Изобретение относится к области металлургии, а именно к низколегированной стали для труб нефтепромыслового сортамента. Сталь имеет химический состав, содержащий, в мас.%: С: от 0,56 до 1,00, Si: от 0,05 до 0,50, Mn: от 0,05 до 1,00, Р: не более 0,025, S: не более 0,010, Al: от 0,005 до 0,100, Mo: от 0,40 до 1,00, V: от 0,07 до 0,30, О: не более 0,010, N: не более 0,03, остальное - Fe и неизбежные примеси. Сталь имеет предел текучести, составляющий по меньшей мере 862 МПа, а ширина дифракционного максимума на половине высоты для плоскости [211] кристаллической решетки, полученного измерением рентгеновской дифракции, составляет не более 0,50°. Сталь имеет высокие механические свойства и стойкость к коррозии в сульфидосодержащей среде. 4 н. и 18 з.п. ф-лы, 4 ил., 4 табл., 2 пр.