METHOD OF PRODUCING ULTRAHIGH-STRENGTH SHEET STEEL

FIELD: metallurgy.SUBSTANCE: to provide high strength properties of sheets at maintaining sufficient ductility and impact viscosity of method involves production of continuously cast slab, heating, hot rolling, hardening and tempering sheets, continuously cast slab is made from steel of following chemical composition, wt%: 0.40-0.47 C; 0.20-0.50 Si; 0.50-0.90 Mn; 0.40-0.80 Cr; 1.80-2.30 Ni; 0.30-0.50 Mo; 0.02-0.06 V; 0.02-0.08 Al; 0.001-0.010 N; 0.10-0.20 Cu; 0.002-0.020 Nb; 0.002-0.015 Ti; 0.001-0.005 B; not more than 0.005 S; not more than 0.010 P; Fe the rest, tempering is performed at temperature of 930-980°C, tempering at temperature of 170-200°C.EFFECT: production of a new highly efficient type of metal - rolled plates of ultra-high strength low-alloy steel bulletproof protection for vehicle body.1 cl, 3 tbl, 1 ex Изобретение относится к области черной металлургии, в частности к производству нового высокоэффективного вида металлопродукции - толстолистового проката из сверхвысокопрочной низколегированной стали для противопульной защиты корпуса транспортных средств. Для обеспечения высоких прочностных свойств листов при сохранении достаточной пластичности и ударной вязкости способ включает получение непрерывнолитого сляба, его нагрев, горячую прокатку, закалку и отпуск листов, при этом непрерывнолитой сляб получают из стали следующего химического состава, мас. %: 0,40-0,47 C; 0,20-0,50 Si; 0,50-0,90 Mn; 0,40-0,80 Cr; 1,80-2,30 Ni; 0,30-0,50 Mo; 0,02-0,06 V; 0,02-0,08 Al; 0,001-0,010 N; 0,10-0,20 Cu; 0,002-0,020 Nb; 0,002-0,015 Ti; 0,001-0,005 B; не более 0,005 S; не более 0,010 P; остальное Fe, закалку осуществляют при температуре 930-980°C, отпуск при температуре 170-200°C. 3 табл., 1 пр.