INCREASING LIFE AND HARDNESS OF ROD- AND PIPE-TYPE REINFORCEMENTS

FIELD: process engineering.SUBSTANCE: invention relates to machining of steel machine building and construction structures. Claimed process comprises the steps that follow. Continuously-cast blank is subjected at the rolling mill stand to helical knurling of outer profile skew profile with the ledge height equal to half it pitch at hot knurling end temperature of 950-1050°C. Screw blank is quenched and rerolled at the rolling mill at a cold state. Then, the surface of screw blanks is degreased and zinc-plated at zinc flow rate of 0.01-0.013 g/m. Now, the iron-zinc coat surface is processed at 420-500°C for 10-20 min.EFFECT: higher rust resistance, endurance and longer life.2 cl, 4 dwg Изобретение относится к повышению технического ресурса, выносливости и технологичности формирования винтовых соединений стальных машиностроительных и строительных конструкций. Способ изготовления стержневой и трубчатой арматуры из высокопрочной коррозионно-стойкой стали включает следующие операции: на непрерывно-литую заготовку в клети прокатного стана по спирали накатывают внешний профиль косой поперечно-винтовой накаткой с высотой рифов, равной половине их шага, при температуре конца горячей накатки 950-1050°C, закаливают полученную винтовую заготовку и осуществляют повторную обкатку на прокатном стане в холодном состоянии, затем поверхность винтовых заготовок обезжиривают, оцинковывают горячим электрохимическим покрытием с расходом цинка 0,01-0,013 г/ми термически обрабатывают поверхность железоцинкового покрытия при температуре 420-500°C в течение 10-20 мин. Технический результат: повышение коррозионной стойкости арматуры, в том числе внутри железобетонной конструкции в зоне контакта с бетоном, повышение выносливости и технического ресурса арматуры. 1 з.п. ф-лы, 4 ил.