METHOD FOR PRODUCING CRYSTALLINE TITANOSILICATE

FIELD: chemistry.SUBSTANCE: initial framework titanosilicate Na(Na,H)TiO[SiO]·2HO is processed with 0.01-0.4 M hydrochloric acid solution for 0.5-2 hours to produce crystalline layered titanosilicate Ti(OH)[SiO(OH)](HO). Further, it is modified by processing with 0.001-0.01 M silver nitrate or caesium chloride solution for no more than 24 hours at pH 6-12 while stirring. A titanosilicate solid phase is separated by centrifugation, washed with deionised water at solid:liquid = 1:(3-5) and dried at temperature 70-100°C. Crystalline layered titanosilicate (Me,H)TiO[SiO]·nHO is produced, wherein Me is silver or caesium, m = 0.1-1.0, n = 0.5-1.8.EFFECT: invention enables producing intercalated framework caesium and silver titanosilicates having high recoverability and iodine sorption capacity.4 cl, 5 ex Изобретение может быть использовано при получении сорбентов для очистки воды от токсичных неорганических веществ. Исходный каркасный титаносиликат Na(Na,H)TiO[SiO]·2HO обрабатывают 0,01-0,4 М раствором соляной кислоты в течение 0,5-2 часов с получением кристаллического слоистого титаносиликата Ti(OH)[SiO(OH)](HO). Затем титаносиликат подвергают модифицированию путем обработки 0,001-0,01 М раствором нитрата серебра или хлорида цезия в течение не более 24 часов при рН 6-12 и перемешивании. Выделяют титаносиликатную твердую фазу центрифугированием, промывают деионизированной водой при Т:Ж=1:(3-5) и сушат при температуре 70-100°С. Получают кристаллический каркасный титаносиликат (Me,Н)TiO[SiO]·nHO, где Me - серебро или цезий, m=0,1-1,0, n=0,5-1,8. Изобретение позволяет получить интеркалированные каркасные титаносиликаты цезия и серебра с высокой регенерируемостью и сорбционной емкостью по иоду 13,84 и 14,1 мг/г, что соответствует степени извлечения 48,4 и 49,3%. 3 з.п. ф-лы, 5 пр.