METHOD OF GROWING SODIUM-BISMUTH MOLYBDATE MONOCRYSTALS

FIELD: chemistry.SUBSTANCE: invention relates to the field of the chemical technology of growing sodium-bismuth molybdate NaBi(MoO)crystals for the research of physical properties and practical application. The monocrystals NaBi(MoO)are grown by crystallisation from a high-temperature solution in a charge melt, which contains sodium-bismuth molybdate and a solvent sodium dimolybdate in a ratio, equal to 10-30:90-70 mol% respectively, crystallisation is carried out on inoculum, oriented perpendicularly to dipyramide edges [101], with the inoculum revolving at a rate of 10-30 rev/min and a rate of extension of 1-5 mm/day, with constant cooling of the solution-melt at a rate of 0.5-15 degrees/day, with growing being carried out under conditions of low gradients ?T/?l lower than 1 degree/cm in the solution-melt.EFFECT: method makes it possible to obtain colourless, stoichiometric in the structure, large (size 75×30 mm), optically homogenous NaBi(MoO)crystals.1 ex Изобретение относится к области химической технологии выращивания кристаллов натрий-висмутового молибдата NaBi(MoO)для исследования физических свойств и практического использования. Монокристаллы NaBi(MoO)выращивают путем кристаллизации из высокотемпературного раствора в расплаве шихты, содержащей натрий-висмутовый молибдат и растворитель димолибдат натрия в соотношении, равном 10-30:90-70 мол.% соответственно, кристаллизацию ведут на затравку, ориентированную перпендикулярно грани дипирамиды [101], при вращении затравки со скоростью 15-30 об/мин и скорости вытягивания 1-5 мм/сутки, при постоянном охлаждении раствора-расплава со скоростью 0,5-15 град/сутки, при этом выращивание ведут в условиях низких градиентов ΔT/Δl менее 1 град/см в растворе-расплаве. Способ позволяет получать бесцветные, стехиометричные по структуре, крупные (размерами 75×30 мм), оптически однородные кристаллы NaBi(MoO). 1 пр.