CONCRETE MIXTURE FOR PRODUCING HEAT-RESISTANT FIRE-RETARDANT COATING

FIELD: construction.SUBSTANCE: concrete mixture for producing heat-resistant fire-retardant coating comprises the components in the following amount (in kg per 1 mof concrete mixture): artificial cement - 400; ground shungite - 50; asbestos - 15; granulated blast-furnace slag - 930; water - 295. At that, the granulated blast-furnace slag has fineness modulus M= 2.98 and bulk density of 500 kg/m, and shungite has optimum dispersion: fineness modulus M= 1.43, specific surface S= 320 m/kg.EFFECT: development of composition of concrete mixture for producing the fire-retardant coating of high thermal stability, having the improved physical and mechanical properties and allowing to improve the degree of fire resistance of reinforced concrete structures.3 tbl Изобретение относится к строительным материалам, в частности к бетонным смесям, обеспечивающим повышение предела огнестойкости железобетонных конструкций. Технический результат - разработка состава бетонной смеси для получения огнезащитного покрытия повышенной термостойки, имеющего улучшенные физико-механические характеристики и позволяющего повысить предел огнестойкости железобетонных конструкций. Бетонная смесь для получения термостойкого огнезащитного покрытия включает компоненты в следующем количестве (в кг на 1 мбетонной смеси): портландцемент - 400; молотый шунгит - 50; асбест - 15; доменный гранулированный шлак - 930; вода - 295. При этом доменный гранулированный шлак имеет модуль крупности M=2,98 и насыпную плотность 500 кг/м, а шунгит имеет оптимальную дисперсность: модуль крупности M=1,43, удельная поверхность S=320 м/кг. 3 табл.