COLD-ROLLED STEEL PLATE HAVING EXCELLENT QUALITY OF SURFACE AFTER FORMING, AND ITS MANUFACTURING METHOD

FIELD: metallurgy.SUBSTANCE: after forming, due to exclusion of formation of linear structures, steel containing the following (wt %) is made: 0.0005-0.0050 C, not more than 0.30 Si, not more than 0.50 Mn, not more than 0.050 P, not more than 0.020 S, 0.010-0.100 Ti and not more than 0.080 solAl, not more than 0.007 N and Fe and inevitable impurities are the rest provided that content of C, N, S and Ti meets the following ratio (I): ([%Ti]/48-[%N]/14-[%S]/32)/([%C]/12)?1.00?(I), where [%M] represents content in the steel of element M (wt %); it is subject to hot rolling, etching, cold rolling, continuous annealing and cooling at the rate not exceeding 30?C/s at the temperature interval of 400-200°C.EFFECT: improving steel plate surface quality.5 cl, 2 tbl Изобретение относится к области металлургии, в частности производству холоднокатаного стального листа для изготовления внешних и внутренних панелей автомобилей. Для повышения качества поверхности стального листа после штамповки за счет исключения образования линейных структур выплавляют сталь, содержащую, мас.%: 0,0005-0,0050 С, не более 0,30 Si, не более 0,50 Мn, не более 0,050 Р, не более 0,020 S, 0,010-0,100 Ti, не более 0,080 sol. Al, не более 0,007 N и остальное - Fe и неизбежные примеси, при условии, что содержание С, N, S и Ti удовлетворяет следующему соотношению (I): ([%Ti]/48-[%N]/14-[%S]/32)/([%C]/12)≥1,00...(I), где [%М] представляет содержание в стали элемента М (мас.%), подвергают горячей прокатке, травлению, холодной прокатке, непрерывному отжигу и охлаждению со скоростью, не превышающей 30˚C/с, в интервале температур 400-200˚C. 3 н. и 2 з.п. ф-лы, 2 табл.