METHOD OF PRODUCING SILICATE GLASS WITH AMORPHOUS SILICON DIOXIDE-BASED REINFORCEMENT COATING

FIELD: chemistry.SUBSTANCE: method includes synthesis of SiOsol, depositing SiOparticles on silicate glass and heat treatment of the coated glass. An amorphous SiObased coating is applied by immersing silicate glass into SiOsol synthesised via hydrolysis of tetraethoxysilane using acetic acid (CHCOOH) as a synthesis reaction catalyst in a medium of ethyl alcohol (CHOH) in molar ratio of components tetraethoxysilane/HO/CHOH/CHCOOH=0.05-0.25/0.95-2/2-16/0.05-0.25. The glass is drawn from the silicon dioxide sol at a controlled rate of 50 to 250 mm/min, followed by isothermal holding of the glass at a temperature of 500±10 to 600±10°C for 15±5 min.EFFECT: method of producing glass with an amorphous silicon dioxide-based reinforcement coating.2 ex Изобретение относится к упрочняющим и защитным покрытиям для силикатного стекла и может быть использовано в стекольной промышленности. Техническим результатом изобретения является разработка способа получения стекла с упрочняющим покрытием на основе аморфного диоксида кремния. Способ включает синтез золя SiO, нанесение частиц SiOна силикатное стекло, термообработку стекла с покрытием. Покрытие на основе аморфного SiOнаносят методом окунания силикатного стекла в золь SiO, синтезированный путем гидролиза тетраэтоксисилана (ТЭОС) с использованием уксусной кислоты (СНСООН) в качестве катализатора реакций синтеза в среде этилового спирта (СНОН) при молярном соотношении компонентов ТЭОС/HO/CHOH/СНСООН=0.05-0.25/0.95-2/2-16/0.05-0.25. Вытягивание стекла из золя диоксида кремния осуществляют с контролируемой скоростью от 50 до 250 мм/мин, с последующей изотермической выдержкой стекла при температуре от 500±10 до 600±10°С в течение 15±5 мин. 2 пр.