METHOD OF MANUFACTURING INTRAOSSEOUS DENTAL IMPLANT

FIELD: medicine.SUBSTANCE: sandblasting processing of an implant surface with particles of aluminium oxide is carried out. Layer-by-layer sputtering by a plasma method of a system of biocompatible coatings from a mixture of titanium or titanium hydride and calcium hydroxyapatite is performed onto the implant base. A discrete layer of disperse powder particles with the surface density of particle inclusions of 10÷15 particles/dmis applied in a remote way on the multilayered system of coatings. As the disperse powder used is aluminium oxide with dispersity of 80-100 mcm.EFFECT: increased mechanical properties of the surface of the biologically active implant layer.2 cl, 1 dwg, 1 tbl Изобретение относится к области медицинской техники, а именно к ортопедической стоматологии, и может быть использовано при изготовлении внутрикостных стоматологических имплантатов путем нанесения на их металлическую основу многослойных плазменных покрытий. Проводят пескоструйную обработку поверхности имплантата частицами оксида алюминия. Осуществляют послойное напыление плазменным методом на основу имплантата системы биосовместимых покрытий из смеси порошков титана или гидрида титана и гидроксиапатита кальция. На многослойную систему покрытий дистанционно наносят плазменным методом дискретный слой из частиц дисперсного порошка с поверхностной плотностью вкрапления частиц 10÷15 частиц/дм. При этом в качестве дисперсного порошка используют оксид алюминия с дисперсностью 80-100 мкм. Способ за счет нанесения на многослойную систему дискретного слоя из частиц дисперсного порошка позволяет повысить механические свойства поверхности биологически активного слоя имплантата. 1 з.п.ф-лы, 1 ил., 1 табл.