METHOD OF OBTAINING CHARGE FOR COMPOSITE MATERIAL BASED ON CALCIUM CARBONATE AND HYDROXYAPATITE AND/OR CARBONATE HYDROXYAPATITE FOR RECOVERY OF BONE TISSUE IN RECONSTRUCTIVE-PLASTIC OPERATIONS

FIELD: chemistry.SUBSTANCE: method includes obtaining a charge for sintering ceramic materials from a powder, synthesised by precipitation of salts in water solutions, with a component ratio: 60-95 wt % of calcium carbonate and 5-40 hydroxyapatite and/or carbonate hydroxyapatite. The claimed method also includes additional milling of the obtained powder and introduction into the powder before and after milling of sodium carbonate in an amount of 0.25-5.0 wt %, taken with respect to calcium carbonate and hydroxyapatite and/or carbonate hydroxyapatite.EFFECT: obtaining a composite ceramic material with higher compression strength and lower porosity.1 tbl, 4 ex Изобретение относится к способу получения шихты для композиционного материала на основе карбоната кальция - гидроксиапатита и/или карбонатгидроксиапатита для восстановления костной ткани при реконструктивно-пластических операциях. Заявленный способ включает получение шихты для спекания керамических материалов из синтезированного путем осаждения солей в водных растворах порошка при соотношении компонентов: 60-95 масс.% карбоната кальция и 5-40 гидроксиапатита и/или карбонатгидроксиапатита. Также заявленный способ включает дополнительный помол полученного порошка и введение в порошок до или после помола карбоната натрия в количестве 0,25-5,0 масс.%, взятого по отношению к карбонату кальция и гидроксиапатиту и/или карбонатгидроксиапатиту. Изобретение направлено на получение композиционного керамического материала с более высокой прочностью при сжатии - 305-590 МПа, и меньшей пористостью - менее 0,5%. 1 табл., 4 пр.