PLATE STEEL MAKING METHOD

FIELD: metallurgy.SUBSTANCE: rear layer plate is made from steel containing the following, wt %: 0.12-0.18 C, 0.10-0.19 Si, 1.2-1.6 Mn, 1.0-1.4 Ni, 0.25-0.45 Mo, 0.02-0.06 Al, 0.02-0.16 Ti, 0.001-0.032 Ca, 0.005- 0.015 P, not more than 0.01 S, and Fe is the rest; with that, total content of Si+P does not exceed 0.21 wt %, hot rolling of plates is performed both in transverse and longitudinal directions with total reduction of cross-sectional area in each of the directions of not less than 50%, rolling is finished at the temperature of 930-1050°C and plates are cooled with water from that temperature, and annealing is performed at the temperature of 250-460°C.EFFECT: improving armour characteristics of protective armour design.3 tbl Изобретение относится к металлургии, конкретнее к технологии производства листовой стали, используемой в качестве тыльного слоя двухслойной разнесенной бронезащитной конструкции. Для повышения бронестойкости бронезащитной конструкции лист тыльного слоя изготавливают из стали, содержащей, мас.%: 0,12-0,18 C; 0,10-0,19 Si; 1,2-1,6 Mn; 1,0-1,4 Ni; 0,25-0,45 Mo; 0,02-0,06 Al; 0,02-0,16 Ti; 0,001-0,032 Ca; 0,005-0,015 P; не более 0,01 S; остальное Fe, причем суммарное содержание Si+P не превышает 0,21 мас.%, горячую прокатку листов ведут как в поперечном, так и в продольном направлениях с суммарным относительным обжатием в каждом из направлений не менее 50%, завершают прокатку при температуре 930-1050°C и с этой температуры листы охлаждают водой, а отпуск проводят при температуре 250-460°C. 3 табл.