METHOD OF APPLYING INSULATING GASKET ON PIPE JOINT

FIELD: chemistry.SUBSTANCE: method is realised by applying a heat shrink multilayer adhesive tape, having a protective layer made from polyethylene tape, electron-chemically modified and aligned in the common direction by 25-75%, and an adhesive layer made from a tape which is electron-chemically mo...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Hauptverfasser:	DZADZAMIJA RUSLAN GIGLOVICH, RAJCHUK FELIKS ZINOV'EVICH, KOLGANOV KONSTANTIN ANATOL'EVICH, TATARENKO OLEG FEDOROVICH
Format:	Patent
Sprache:	eng ; rus
Schlagworte:	ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE ADHESIVES BLASTING CHEMICAL PAINT OR INK REMOVERS CHEMISTRY COATING COMPOSITIONS, e.g. PAINTS, VARNISHES ORLACQUERS CORRECTING FLUIDS DYES ENGINEERING ELEMENTS AND UNITS FILLING PASTES GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVEFUNCTIONING OF MACHINES OR INSTALLATIONS HEATING INKS JOINTS OR FITTINGS FOR PIPES LIGHTING MEANS FOR THERMAL INSULATION IN GENERAL MECHANICAL ENGINEERING METALLURGY MISCELLANEOUS APPLICATIONS OF MATERIALS MISCELLANEOUS COMPOSITIONS NATURAL RESINS NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL PAINTS PASTES OR SOLIDS FOR COLOURING OR PRINTING PIPES POLISHES SUPPORTS FOR PIPES, CABLES OR PROTECTIVE TUBING THERMAL INSULATION IN GENERAL USE OF MATERIALS AS ADHESIVES USE OF MATERIALS THEREFOR WEAPONS WOODSTAINS
Online-Zugang:	Volltext bestellen
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Beschreibung
Zusammenfassung:	FIELD: chemistry.SUBSTANCE: method is realised by applying a heat shrink multilayer adhesive tape, having a protective layer made from polyethylene tape, electron-chemically modified and aligned in the common direction by 25-75%, and an adhesive layer made from a tape which is electron-chemically modified with accelerated ions with absorbed dose of 0.1 MGy, made from a composition which contains an ethylene and vinyl acetate copolymer with content of vinyl acetate groups of 10-14%, melt fluidity of 5.0-10.0 g/10 min and breaking strength of 9.8 MPa or an ethylene and vinyl acetate copolymer with content of vinyl acetate groups of 10-15%, melt fluidity of 2.0-6.0 g/10 min and breaking strength of 9.0 MPa, mineral filler, modifier - polyisocyante and sulphur-containing polyhydroquinone disulphide stabiliser in concentration of 0.1-0.3 wt %.EFFECT: improved adhesion strength of the insulation material.9 cl, 2 tbl Изобретение относится к области защиты металла от коррозии и может найти применение при защите от коррозии сварных швов металлических трубопроводов, предназначенных для транспортировки жидких и газообразных сред. Способ осуществляют путем нанесения термоусаживающейся многослойной адгезионной ленты, содержащей защитный слой из полиэтиленовой ленты, электронно-химически модифицированной и ориентированной в долевом направлении на 25-75%, и адгезионный слой из ленты, электронно-химически модифицированной ускоренными электронами с поглощенной дозой 0,1 МГр, выполненной из состава, содержащего сополимер этилена с винилацетатом с содержанием винилацетатных групп 10-14%, текучести расплава 5,0-10,0 г/10 мин и прочности при разрыве 9,8 МПа или сополимера этилена с винилацетатом с содержанием винилацетатных групп в пределах 10-15%, текучести расплава 2,0-6,0 г/10 мин и прочности при разрыве 9,0 МПа, минеральный наполнитель, модификатор - полиизоцианат и серусодержащий стабилизатор полигидрохинондисульфид в концентрации 0,1-0,3 мас.%. Технический результат - улучшение адгезионной прочности изоляционного материала. 8 з.п. ф-лы, 2 табл.