METHOD OF PRODUCING SORBENT FOR TRAPPING VOLATILE TYPES OF RADIOACTIVE IODINE

FIELD: process engineering.SUBSTANCE: invention relates to method of producing sorbent for trapping volatile types of radioactive iodine at nuclear power stations in operating and emergency conditions. Proposed method comprises impregnating silica gel, in single-stage process, with solution of silver and nickel nitrates in ammonium or with mix of solution of silver and nickel salts in ammonium. Note here that silver and nickel concentration in solutions is selected so that silver concentration in finished sorbent makes 1.0-2.0 wt % while molar ratio of Ni:Agvaries from 2:1 to 4:1. Then, drying is performed at temperature varying from room temperature to 300°C. Now, holding is performed at said temperature for four hours.EFFECT: faster synthesis, sufficiently high properties. Изобретение относится к производству сорбентов для улавливания летучих форм радиоактивного йода и может быть использовано при изготовлении сорбентов для предотвращения радиоактивного выброса в окружающую среду при эксплуатационных режимах работы и при авариях на атомных электростанциях (АЭС), а также для очистки паровоздушных потоков от летучих соединений радиоактивного йода в технологических схемах по переработке отработавшего ядерного топлива. Способ получения сорбента включает одностадийную пропитку силикагеля раствором азотнокислых солей серебра и никеля в аммиаке или смесью водных растворов солей серебра и никеля с аммиаком. При этом концентрации серебра и никеля в растворах подбирают так, чтобы в готовом сорбенте содержание серебра составляло 1.0-2.0 мас.%, а мольное отношение Ni:Agбыло от 2:1 до 4:1. Затем проводят сушку при подъеме температуры от комнатной до 300°С и выдержку при этой температуре в течение четырех часов. Преимуществом предлагаемого способа получения сорбента является уменьшение времени синтеза при сохранении всех свойств получаемого сорбента.