METHOD FOR FORMING CHITOSAN FILM COATING AND CHITOSAN FILM COATING

FIELD: medicine. ^ SUBSTANCE: chitosan is dissolved in an organic acid: 4-6% citric acid or 2-8% lactic acid in the relation of the ingredients chitosan: the organic acid 1:2-1:4 to prepare a forming solution. Chitosan has molecular weight 80-500 kDa. The forming solution is added with vitamin B1 in the amount of max. 0.5 wt %. The prepared forming solution is applied on a substrate in the amount of 0.2-0.25 ml/cm2 and kept to achieve a film structure. Said method is used to form the chitosan film coating having the thickness of 50-250 mcm and the breaking elongation of 42 to 470%. ^ EFFECT: group of inventions allows preparing high-elastic chitosan citrate or lactate films possessing bactericidal action. ^ 2 cl, 1 tbl, 13 ex Группа изобретений относится к области биохимии и биотехнологии. Растворяют хитозан в органической кислоте: 4-6%-ной лимонной кислоте или 2-8%-ной молочной кислоте, при соотношении компонентов хитозан: органическая кислота 1:2-1:4 и получают формовочный раствор. Хитозан используют с молекулярной массой 80-500 кДа. Дополнительно в формовочный раствор вводят витамин В1 в количестве не более 0,5 мас.%. Наносят полученный формовочный раствор на подложку в объеме 0.2-0.25 мл/см2 и выдерживают до достижения пленочной структуры. Указанным способом получают пленочное покрытие на основе хитозана толщиной 50-250 мкм и имеющее величину относительного удлинения при разрыве от 42 до 470%. Группа изобретений позволяет получить высокоэластичные пленки из цитрата или лактата хитозана, обладающие бактерицидным действием. 3 н. и 2 з.п. ф-лы, 1 табл., 13 пр.