METHOD OF PRODUCING TITANIUM CARBOSILICIDE-BASED POWDERED COMPOSITION

FIELD: chemistry. ^ SUBSTANCE: method of producing titanium carbosilicide-based powdered composition involves preparation of a powdered mixture consisting of titanium, silicon carbide and graphite, taken in molar ratio 3:1.25:0.75, mechanical synthesis in an evacuated planetary mill at drum rotational speed of 320 rpm in intermittent mode, cold pressing, heat treatment in a vacuum furnace at temperature 1350C for 3 hours and subsequent grinding of the obtained sample in a planetary mill using titanium equipment to obtain powder of the required particle size. ^ EFFECT: obtaining a powdered composition with high content of titanium carbosilicide without undesirable impurities. ^ 3 ex Изобретение относится к производству керамических составов на основе карбосилицида титана, может быть использовано в машиностроительной и горнодобывающей промышленности, в инструментальном и ремонтном производствах для получения износостойких покрытий деталей узлов трения. Способ получения порошковой композиции на основе карбосилицида титана включает получение порошковой смеси, состоящей из титана, карбида кремния и графита, взятых в мольном соотношении 3:1,25:0,75, механосинтез в планетарной вакуумированной мельнице при частоте вращения барабана 320 об/мин, в прерывистом режиме, холодное прессование, термообработку в вакуумной печи при температуре 1350°C в течение 3 часов и последующий размол полученного образца в планетарной мельнице с применением титановой оснастки до получения порошка нужного размера. Технический результат изобретения - получение порошковой композиции с высоким содержанием карбосилицида титана без нежелательных примесей. 3 пр.