DISPERSANTS IN COMPOSITES

FIELD: chemistry. ^ SUBSTANCE: invention describes a composition containing (a) a polystyrene or polyolefin polymer, (b) talc as filler with average particle size of 0.4-25 mcm, contained in amount of 0.1-10% of the weight of the component (a), and (c) a dispersant which is based on a sorbitan ester, polyethylene-block-polyethylene oxide or an amphiphilic statistical, block or comb-like copolymer, where the copolymer contains C12-C32 alkyl(meth)acrylate. Disclosed also is a method of producing synthetic polymer material, involving mixing in molten state a mixture of said components and using dispersant (c) to disperse talc filler (b) in said polystyrene or polyolefin polymer matrix to obtain composite material. ^ EFFECT: disclosed compositions have higher modulus of elasticity in tension, breaking strength and temperature for thermal deformation under load. ^ 20 cl, 8 tbl, 68 ex В заявке описана композиция, включающая (а) полистирольный или полиолефиновый полимер, (б) тальк в качестве наполнителя со средним размером частиц от 0,4 до 25 мкм, содержащегося в количестве от 0,1 до 10% в пересчете на массу компонента (а), и (в) диспергатор, который основан на сорбитановом сложном эфире, полиэтилен-блок-полиэтиленоксиде или амфифильном статистическом, блочном или гребнеобразном сополимере, где сополимер включает С12-С32 алкил(мет)акрилат. Также представлен способ получения синтетического полимерного материала, включающий смешение в расплаве смеси указанных компонентов и применение диспергатора (в) для диспергирования талькового наполнителя (б) в упомянутой полистирольной или полиолефиновой полимерной матрице с получением композитного материала. Композиции, согласно изобретению, имеют улучшенные модуль упругости при растяжении, предел прочности при разрыве и температуру тепловой деформации под нагрузкой. 2 н. и 18 з.п. ф-лы, 8 табл.