METHOD OF PRODUCING GLASS WITH TITANIUM DIOXIDE BASED COATING

FIELD: chemistry. ^ SUBSTANCE: invention relates to vacuum coating techniques and can be used to obtain photocatalytically active and sun-screening coatings based on titanium dioxide. The method is realised by forming a coating containing doped ions of at least one of the following elements: Ni, Co, Fe, Cr, Sb, Sn, V, Mn, Cu, W, Zn, Nb, Zn, N, Si, depositing a titanium dioxide based layer, high-temperature processing at 500-700C and oxidation of multi-layer titanium-containing coatings. During thermal processing, doped ions enter the titanium dioxide layer through diffusion from intermediate layers with thickness of the TiO2 layer equal to 20-100 nm. ^ EFFECT: method of producing TiO2 based coatings with improved functional and operational characteristics owing to formation of a dense crystalline film of TiO2 containing doped ions. ^ 4 cl, 5 tbl, 3 ex Изобретение относится к вакуумным способам нанесения покрытий и может быть использовано для получения фотокаталитически активного и солнцезащитного покрытия на основе диоксида титана. Технической задачей изобретения является разработка способа получения покрытий на основе TiO2 с улучшенными функциональными и эксплуатационными характеристиками за счет формирования плотной кристаллической пленки TiO2, содержащей примесные ионы. Способ осуществляют путем формирования покрытия, содержащего примесные ионы, по крайней мере, одного из элементов ряда: Ni, Co, Fe, Cr, Sb, Sn, V, Мn, Сu, W, Zn, Nb, Zn, N, Si, нанесения слоя на основе диоксида титана, высокотемпературной обработки при температуре 500-700°С и окисления многослойных титаносодержащих покрытий. При термообработке примесные ионы входят в слой двуоксида титана за счет их диффузии из промежуточных слоев при толщине ТiO2 слоя - 20-100 нм. 3 з.п. ф-лы, 5 табл.