METHOD TO JOIN HEAT-RESISTANT COBALT-BASED ALLOY AND CERAMICS BASED ON SILICON NITRIDE

FIELD: technological processes. ^ SUBSTANCE: invention relates to a technology for joining structural elements of products that operate under high thermomechanical loads. The method to join a heat-resistant cobalt-based alloy with ceramics based on silicon nitride includes diffuse welding at temperature of 90010C, pressure of 171 MPa for 180030 s. An intermediate material is previously applied onto welded surfaces. The intermediate material is a mechanical mixture with content of 0.1Ç0.3 wt % Cu, 0.1Ç0.3 wt % Co, the balance is Ni. The strength of the produced compound is âc=1005 MPa. ^ EFFECT: expansion of technological capabilities and increased strength of connection of heat-resistant cobalt-based alloy with ceramics on the basis of silicon nitride. ^ 1 dwg Изобретение относится к технологии соединения конструктивных элементов изделий, работающих в условиях высоких термомеханических нагрузок. Способ соединения жаропрочного сплава на кобальтовой основе с керамикой на основе нитрида кремния включает осуществление диффузионной сварки при температуре 900±10°С, давлении 17±1 МПа в течение 1800±30 с. На свариваемые поверхности предварительно нанесен промежуточный материал. В качестве промежуточного материала используют механическую смесь с содержанием 0,1...0,3 вес. % Сu, 0,1...0,3 вес. % Со, остальное Ni. Прочность полученного соединения составляет σсд100±5 МПа. Техническим результатом является расширение технологических возможностей и повышение прочности соединения жаропрочного сплава на кобальтовой основе с керамикой на основе нитрида кремния. 1 ил.