PROCEDURE FOR PRODUCTION OF MECHANICALLY ALLOYED NITROGEN CONTAINING STEEL

FIELD: metallurgy. ^ SUBSTANCE: mixture of powders of metals is subjected to mechanical alloying in atmosphere of nitrogen. Ratio of weight of metal powder mixture and milling balls amounts to 1:30. Upon mechanical alloying mixture of metal powder is roasted in protective or reducing atmosphere at 400-600C. 2-4 % of nano dimension powder of nickel is added into roasted mixture and mixed. Further, prepared charge is pressed in a mould and is sintered in nitrogen containing atmosphere at temperature 1100-1300C. ^ EFFECT: activation of sintering, reduced time for mechanical alloying, facilitation of high density, strength and wear and corrosion resistance of steel. ^ 2 cl, 1 tbl, 1 ex Изобретение относится к области порошковой металлургии, а именно к производству легированных сталей. Смесь порошков металлов подвергают механическому легированию в атмосфере азота. Соотношение масс смеси металлических порошков и мелющих шаров составляет 1:30. После механического легирования смесь порошков металлов отжигают в защитной или восстановительной атмосферах при 400-600°С, в отожженную смесь добавляют 2-4% наноразмерного порошка никеля и производят перемешивание. Затем готовую шихту прессуют в пресс-форме и спекают в азотсодержащей атмосфере при температурах 1100-1300°С. Способ обеспечивает активацию спекания, сокращение длительности механического легирования, достижение высокой плотности, прочности, износо- и коррозионной стойкости стали. 1 з.п. ф-лы, 1 табл.