PROCEDURE FOR AGEING PARTS OF HIGH PRECISION INSTRUMENTS OUT OF QUENCHED ALLOY AK8M

FIELD: metallurgy. ^ SUBSTANCE: procedure for ageing parts of high precision instruments out of quenched alloy AK8M consists in two-stage ageing and cooling in air. The first stage of ageing is performed during 1.5 hours at temperature 1405C, while the second stage is performed during 3 hours at tem...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Hauptverfasser:	BARSUKOVA OL'GA VIKTOROVNA, EREMIN ANATOLIJ IVANOVICH, AKSENOVA VALENTINA GRIGOR'EVNA, KHARITONOV VIKTOR IVANOVICH
Format:	Patent
Sprache:	eng ; rus
Schlagworte:	CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS ANDNON-FERROUS ALLOYS CHEMISTRY FERROUS OR NON-FERROUS ALLOYS METALLURGY TREATMENT OF ALLOYS OR NON-FERROUS METALS
Online-Zugang:	Volltext bestellen
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Beschreibung
Zusammenfassung:	FIELD: metallurgy. ^ SUBSTANCE: procedure for ageing parts of high precision instruments out of quenched alloy AK8M consists in two-stage ageing and cooling in air. The first stage of ageing is performed during 1.5 hours at temperature 1405C, while the second stage is performed during 3 hours at temperature 1705C. ^ EFFECT: raised strength without reduction of plasticity; upgraded reliability of parts. ^ 1 tbl, 1 ex Изобретение относится к металлургии и может быть применено при термической обработке отливок из сплава АК8М при изготовлении высокоточных деталей. Способ старения деталей высокоточных приборов из закаленного сплава АК8М включает двухступенчатое старение с охлаждением на воздухе. Первую ступень старения проводят в течение 1,5 часов при температуре 140±5°С, а вторую ступень - в течение 3 часов при температуре 170±5°С. Повышается прочность без снижения пластичности и надежность деталей. 1 табл.