GLASS WITH LEAD SELENIDE NANOCRYSTALS FOR NEAR INFRARED ANTIREFLECTION FILTERS

FIELD: chemistry. ^ SUBSTANCE: glass with lead selenide (PbSe) nanocrystals is meant for use in laser engineering as antireflection filters (saturating absorbents, passive shutters) for realising mode synchronisation and q modulation of near infrared lasers. PbSe nanocrystals with size of 3.5-10.0 nm are formed in the glass after thermal treatment of the glass. The glass has the following components in the following ratios, wt %: SiO2 42.0-48.0; B2O3 12.0-16.5; Na2O 15.5-16.5; NaF 1.5-3.0; ZnO 9.0-12.5; Al2O3 3.5-5.5; PbO 3.5-5.5; Se 2.0-3.5. ^ EFFECT: formation of lead selenide nanocrystals with size of 3,5-10 nm for providing spectral absorption and antireflection in the near infrared spectral region between 0,9 and 2,6 mcm. ^ 2 tbl Стекло с нанокристаллами селенида свинца (PbSe) предназначено для использования в лазерной технике в качестве просветляющихся фильтров (насыщающихся поглотителей, пассивных затворов) для реализации режимов синхронизации мод и модуляции добротности лазеров ближнего инфракрасного диапазона. Формирование в стекле нанокристаллов PbSe размером от 3,5 до 10,0 нм достигается в результате термической обработки стекла. Техническая задача изобретения - формирование нанокристаллов селенида свинца размером от 3,5 до 10 нм для обеспечения спектрального поглощения и просветления в ближней ИК области спектра от 0,9 до 2,6 мкм. Стекло включает компоненты при следующем их соотношении, мас.%: SiO2 42,0-48,0; В2O3 12,0-16,5; Na2О 15,5-16,5; NaF 1,5-3,0; ZnO 9,0-12,5; Аl2О3 3,5-5,5; PbO 3,5-5,5; Se 2,0-3.5. 2 табл.