POLYCARBONATES WITH GOOD WETTABILITY

FIELD: chemistry. ^ SUBSTANCE: invention relates to a polycarbonate as substrate material for making transparent moulded articles. The polycarbonate is obtained through phosgenation of bisphenols at temperature 0-40C and 5-17 mol % excess phosgene. The polycarbonate contains carbamate compounds of formula (1) , in which R1 and R2 denote hydrogen or C1-C12alkyl, or R1 and R2 - C4-C12 alkylidene or C4-C5 alkylidene, R3 and R4 denote hydrogen C1-C12 alkyl, mainly C1-C8 alkyl, phenyl, or R3 and R4, bonded to a carbon atom, together form cyclohexyl or trimethylcyclohexyl, R5 denotes hydrogen, C1-C12 alkyl, C5-C12 cycloalkyl, phenyl or cumyl. ^ EFFECT: invention enables to obtain polycarbonate with low content of carbamate compound impurities equal to 0,2-300 parts per million. ^ 9 cl, 1 tbl, 8 ex Изобретение относится к поликарбонату в качестве материала-подложки для изготовления прозрачных литых изделий. Поликарбонат получают фосгенированием бисфенолов при температуре от 0 до 40°C с избытком фосгена от 5 до 17 мол.%. Поликарбонат содержит карбаматные соединения формулы (1) ! ! в которой R1 и R2 - водород или C1-C12алкил, преимущественно метил, этил, пропил, изопропил или бутил, или R1 и R2 - C4-C12алкилиден, преимущественно С4-С8алкилиден или С4-С5алкилиден, R3 и R4 - водород, C1-C12алкил, преимущественно C1-C8алкил, или фенил, или R3 и R4 вместе, связанные с атомом углерода, образуют циклогексил или триметилциклогексил, R5 - водород, C1-C12алкил, C5-C12циклоалкил, фенил или кумил, преимущественно водород, трет-бутил или кумил. Изобретение позволяет получить поликарбонат с более низким содержанием примесей карбаматных соединений, равным от 0,2 до 300 ч./млн. 8 з.п. ф-лы, 1 табл.