RAW MATERIAL MIXTURE

FIELD: chemistry. ^ SUBSTANCE: invention relates to field of construction materials and can be used as thin-layered hydroinsulation protective coating of concrete and other porous surfaces in industrial and civil construction. Raw material mixture contains, wt %: Portland cement 30.3-32.3, sand with maximal fraction size 0.63 mm 40.4-40.9, finely milled dolomitic limestone with specific surface equal 200 m2/kg, 8.1-8.6, complex additive 3.2-3.7, water 16.0-16.5, said complex additive contains, wt %: microsilica with specific surface equal 2000 m2/kg, 47-49, alumina cement 24.5-25.0, gypsum CaSO42H2O 9.8-10.2, plasticiser C-3 3.7-4.0, silicic acid sol H4SiO4 with density 1.014 g/cm3 and pH=3.50.5 3.0-3.4, bentonite clay with specific surface equal 500 m2/kg, 10.0-10.4. ^ EFFECT: reduction of unmixing, increase of water-holding capacity, reduction of water absorption, increase of protective coating compression strength. ^ 1 tbl Изобретение относится к области строительных материалов и может быть использовано в качестве тонкослойного гидроизоляционного защитного покрытия бетонных и других пористых поверхностей в промышленном и гражданском строительстве. Технический результат - уменьшение расслаиваемости, повышение водоудерживающей способности, уменьшение водопоглощения, повышение прочности на сжатие защитного покрытия. Сырьевая смесь содержит, мас.%: портландцемент 30,3-32,3, песок с максимальным размером фракций 0,63 мм 40,4-40,9, тонкомолотый доломитизированный известняк с удельной поверхностью, равной 200 м2/кг, 8,1-8,6, комплексную добавку 3,2-3,7, воду 16,0-16,5, причем указанная комплексная добавка содержит, мас.%: микрокремнезем с удельной поверхностью, равной 2000 м2/кг, 47-49, глиноземистый цемент 24,5-25,0, гипс CaSO4·2H2O 9,8-10,2, пластификатор С-3 3,7-4,0, золь кремниевой кислоты H4SiO4 плотностью 1,014 г/см3 и рН 3,5±0,5 3,0-3,4, бентонитовая глина с удельной поверхностью, равной 500 м2/кг, 10,0-10,4. 1 табл.