WATER CYANIDE-BEARING COMPOSITION FOR LEACHING OF METALS FROM ITS CONTAINING MATERIALS

FIELD: metallurgy. ^ SUBSTANCE: particular invention relates to cyanides leaching of metals, particularly to water cyanide-bearing composition for leaching of metals from its containing materials. Composite contains at least one non-ionic surface active agent. This surface active agent in water solution regulated by means of NaOH up to value of pH from 9.8 up to 10.2, in concentration from 0.01 up to 0.2% wt, at temperature 23C leads to reduction of angle of capillarity on glass after 1 second to at least 10. Composite can additionally at least one cationic surface active agent and/or at least one anionic surface active agent. ^ EFFECT: reduction of duration of leaching and amount of cyanide. ^ 11 cl, 4 tbl Данное изобретение относится к цианидному выщелачиванию металлов, в частности к водной цианидсодержащей композиции для выщелачивания металлов из содержащих их материалов. Композиция содержит, по меньшей мере, одно неионное поверхностно-активное вещество. Это поверхностно-активное вещество в водном растворе, регулируемом с помощью NaOH до значения рН от 9,8 до 10,2, в концентрации от 0,01 до 0,2% масс. при температуре 23°С приводит к уменьшению краевого угла на стекле через 1 секунду на, по меньшей мере, 10°. Композиция может дополнительно включать по меньшей мере, одно катионное поверхностно-активное вещество и/или, по меньшей мере, одно анионное поверхностно-активное вещество. Техническим результатом является сокращение продолжительности выщелачивания и количества цианида. 10 з.п. ф-лы, 4 табл.