METHOD FOR PREPARATION OF IRON OXIDE PIGMENT FROM SPECULARITE

FIELD: chemistry. ^ SUBSTANCE: method for preparation of iron oxide pigment from specularite includes specularite milling up to particle size more than 1 mm - 5 mm, after material concentration with magnetic separation up to content of -Fe2O3 more than 60.0 wt % specularite is concentrated again. Concentrated specularite can serve as starting material for obtaining of pigment with dull luster consisting of iron mica with Fe2O3 content more than 85 wt % which includes thin scaly plates in amount more than 50 wt % and is featured with residue after wet sieving on a sieve with mesh size 63 mcm not more than 35 wt %. ^ EFFECT: invention allows to obtain pigments from specularite for protective-decorative and decorative coatings. ^ 8 cl, 2 tbl, 5 ex Изобретение относится к получению железоокисных пигментов и может быть использовано в лакокрасочной промышленности, производстве строительных материалов, пластмасс, резинотехнических изделий. В способе получения железоокисного пигмента из спекулярита сначала ведут измельчение спекулярита до размера частиц более 1 мм - 5 мм, затем проводят обогащение методом магнитной сепарации до содержания α-Fе2О3 более 60,0 мас.%, после чего обогащенный спекулярит снова измельчают. Из обогащенного спекулярита может быть получен пигмент с матовым блеском, состоящий из железной слюдки с содержанием Fе2О3 более 85 мас.%, которая включает тонкие чешуйчатые пластинки в количестве более 50 мас.%, и характеризующийся остатком после мокрого просеивания на сите с размером отверстий 63 мкм не более 35 мас.%. Изобретение позволяет получить из спекулярита пигменты для защитно-декоративных и декоративных покрытий. 2 н. и 6 з.п. ф-лы, 2 табл.