ARMOURED STEEL AND STEEL ARMOURED DETAIL

FIELD: metallurgy. ^ SUBSTANCE: invention relates to ferrous metallurgy and armor protection and can be used for manufacturing of personal protection equipment and also for armor protection of cars, special carriages and other lightly armoured machinery. Steel contains carbon, silicon, manganese, chromium, nickel, molybdenum, vanadium, sulfur, phosphor, niobium, copper and iron, at following ratio of components , wt %: carbon 0.47 - 0.52, silicon 0.50 - 0.80, manganese 0.30 - 0.50, chromium 1.20 - 1.50, nickel 0.90 - 1.20, molybdenum 0.75 - 0.85, vanadium 0.18 - 0.28, niobium 0.02 - 0.05, copper ëñ 0.30, sulfur ëñ 0.01, phosphor ëñ 0.01, iron is the rest. ^ EFFECT: increasing of persistence of armor protection facilities, ballisticproof and fragmentation protective in combination with reduced inclination for forming of secondary debris with influence of modern weapons. ^ 2 cl, 2 tbl Изобретение относится к области черной металлургии и бронезащиты и может быть использовано при изготовлении средств индивидуальной защиты, а также для бронезащиты автомобилей, спецвагонов и других легкобронированных машин. Сталь содержит углерод, кремний, марганец, хром, никель, молибден, ванадий, серу, фосфор, ниобий, медь и железо, при следующем соотношении компонентов, мас.%: углерод 0,47-0,52, кремний 0,50-0,80, марганец 0,30-0,50, хром 1,20-1,50, никель 0,90-1,20, молибден 0,75-0,85, ванадий 0,18-0,28, ниобий 0,02-0,05, медь ≤0,30, сера ≤0,01, фосфор ≤0,01, железо остальное. Повышается живучесть средств бронезащиты, противопульная и противоосколочная стойкость в сочетании с пониженной склонностью к образованию вторичных осколков при воздействии современных средств поражения. 2 н.п. ф-лы, 2 табл.