PROCESS FOR PREPARING SILICON CARBIDE

FIELD: processes for preparing powdery silicon carbide used in powder metallurgy for the manufacture of heat resistant ceramic wares and abrasive pastes which are resistant to aggressive media. SUBSTANCE: the silicon-containing raw materials (silica, quartzite and diatomite) are mixed with carbon and magnesium, the ratio of the components being as follows (wt %): 45-55 silicon-containing raw material; 9-11 carbon; 36-44 magnesium. The mixture is rammed to a density of 1.04-1.63 g/cmand charged into a self-propagating high-temperature synthesis reactor. The reactor is sealed, filled with argon and the combustion process is initiated at 1400-2200 C. EFFECT: improved homogeneity of the granulometric composition of the products. 1 tbl Изобретение относится к способам получения порошкообразного карбида кремния, применяемого в порошковой металлургии для изготовления жаропрочных и стойких к агрессивным средам керамических изделий и абразивных паст, и позволяет повысить однородность продукта по гранулометрическому составу. Смешивают кремнеземсодержащее сырье (кремнезем, кварцит, диатомит) с углеродом и магнием при следующих соотношениях компонентов, мас.%: кремнеземсодержащее сырье 45 - 55, углерод 9 - 11, магний 36 - 44. С�есь трамбуют до плотности 1,04 - 1,63 г/сми загружают в реактор самораспространяющегося высокотемпературного синтеза, его герметизируют, заполняют аргоном и инициируют процесс горения при 1400 - 2200°С. 1 табл.