PROCESS FOR PREPARING A COMPOSITE FRICTION MATERIAL WITH IRON BASE

The invention relates to a process for preparing a composite friction material with iron base intended for car friction pads or other industrial friction applications. According to the invention, the process starts by screening the iron, copper and titanium dioxide powders having a particle size of less than 10 μ m, after which the powder mixture dosed according to the formula is homogenized by mechanical grinding, for 15 min, in a planetary ball mill having a plate rotary speed of 1000 rpm and the containers rotary speed of 500 rpm, the homogenized mixture being then compressed biaxially in a closed mould, using a compacting pressure of 600 MPa, in the final stage the raw pressed pieces being sintered under vacuum, at a pressure of 10torr, at a sintering temperature of 1050°C, the sintering temperature being maintained for 30 min. Invenţia se referă la un procedeu de elaborare a unui material compozit de fricţiune cu baza fier, destinat realizării unor plăcuţe de frână pentru autoturisme sau pentru alte aplicaţii industriale de fricţiune. Procedeul conform invenţiei începe cu sortarea pulberilor de fier, cupru şi dioxid de titan cu dimensiunea particulelor mai mică de 10 μ m, după care amestecul de pulberi dozat după reţetă se omogenizează prin măcinare mecanică, timp de 15 min, într-o moară planetară cu bile, având turaţia platanului de 1000 rot/min şi turaţia containerelor de 500 rot/min, apoi amestecul omogenizat se presează biaxial, într-o matriţă închisă, utilizând o presiune de compactizare de 600 MPa, iar în ultima etapă piesele presate, crude, sunt sinterizate în vid la o presiune de 10torr, la o temperatură de sinterizare de 1050°C, durata de menţinere a temperaturii de sinterizare fiind de 30 min.