POLYMER COMPOSITIONS FOR ROTATIONAL MOLDING APPLICATIONS

A polymer having a density of from about 0.94 g/ cm3 to about 0.96 g/ cm3 and a primary structure parameter 2 (PSP2 value) of greater than about 8.5, wherein an article formed from the polymer has an environmental stress crack resistance of equal to or greater than about 1000 hours when measured in accordance with ASTM D 1693 condition A. A polymer having at least one lower molecular weight component and at least one higher molecular weight component and having a PSP2 value of equal to or greater than about 8.5, wherein an article formed from the polymer has an environmental stress crack resistance of greater than about 1000 hours when measured in accordance with ASTM D 1693 condition A. Un polímero que tiene una densidad de aproximadamente 0.94 g/cm3 a aproximadamente 0.96 g/cm3 y un parámetro de estructura primaria 2 (valor PSP2) de más de aproximadamente 8.5, en donde un artículo formado por el polímero tiene una resistencia a las grietas de tensión ambiental de igual a o mayor que aproximadamente 1000 horas cuando se mide de acuerdo con ASTM D1693 condición A. Un polímero que tiene al menos un componente de peso molecular más bajo y por lo menos un componente de peso molecular más alto y que tiene un valor de PSP2 igual o superior a aproximadamente 8.5, en donde un artículo formado por el polímero tiene una resistencia a las grietas de tensión ambiental de más de aproximadamente 1000 horas cuando se mide de acuerdo con ASTM D 1693 condición A.