POLYETHYLENE COPOLYMER WITH BROAD SHORT CHAIN BRANCHING DISTRIBUTION

A polyethylene copolymer comprising ethylene units and C4 to C8 α-olefin comonomer units having the following characteristics: a melt index from about 0.1 to about 15 g/10 min as determined at 190°C by ASTM D1238 under 2.16 kg and at 190°C; a density from 0.905 to 0.930 g/cc; a molecular weight distribution from about 1.5 to about 2.7; a Crystallization Elution Fractionation temperature range excluding the first 10% and the last 1% polymer on the temperature scale following the equation: οΤ [°C] â¿¥ -909* (density [g/cc]) + 863; and a lamellar thickness distribution following the equation: F %â¿¥ 510 * (density [g/cc] -0.905), where F % is the percentage of lamellar thickness greater than 12 nm. Un copolímero de polietileno que comprende unidades de etileno y unidades de comonómero de a-olefina C4 a C8 que tienen las siguientes características: un índice de fusión de aproximadamente 0.1 a aproximadamente 15 g/10 min según lo determinado a 190 °C por ASTM D1238 bajo 2.16 kg y a 190 °C; una densidad de 0.905 a 0.930 g/cm3; una distribución de peso molecular de aproximadamente 1.5 a aproximadamente 2.7; un rango de temperatura de fraccionamiento por elución de cristalización que excluye el primer 10 % y el último 1 % de polímero en la escala de temperatura siguiendo la ecuación: ?T [°C] = -909*(densidad [g/cm3]) + 863; y una distribución de grosor lamelar siguiendo la ecuación: F % = 510 * (densidad [g/cm3] -0.905), en donde F % es el porcentaje de espesor lamelar mayor de 12 nm.