NON-ORIENTED ELECTRICAL STEEL SHEET AND MANUFACTURING METHOD THEREFOR

A non-oriented electrical steel sheet according to one embodiment of the present invention comprises, by wt%, 0.005% or less of C (excluding 0%), 1.2-2.7% of Si, 0.4-2.0% of Mn, 0.005% or less of S (excluding 0%), 0.3% or less of Al (excluding 0%), 0.005% or less of N (excluding 0%), 0.005% or less of Ti (excluding 0%), and the balance of Fe and inevitable impurities, wherein the following formula 1 is satisfied, and, in the steel sheet, the volume fraction of grains, in which the angle between {112} plane and a rolling plane is 15° or less, is 40-60%. [Formula 1] 0.3 ⿤ ([Si]+ [Al]-1.5)/[Mn] ⿤ 0.85 (In formula 1, [Si] and [Al], [Mn] represent the amounts (wt%) of Si, Al and Mn, respectively.). Una chapa de acero eléctrico no orientado según una realización de la presente invención comprende, en % en peso, 0.005 % o menos de C (excluyendo 0 %), del 1.2 al 2.7 % de Si, del 0.4 al 2.0 % de Mn, 0.005 % o menos de S (excluyendo 0 %), 0.3 % o menos de Al (excluyendo 0 %), 0.005 % o menos de N (excluyendo 0 %), 0.005 % o menos de Ti (excluyendo 0 %), y el resto de Fe e impurezas inevitables, en donde se cumple la siguiente Fórmula 1, y, una fracción de volumen de granos que tengan un ángulo de 15° o menos entre un plano {112} y un plano de laminación en la chapa de acero es del 40 al 60 %. [Fórmula 1] 0.3 = ([Si]+ [Al]-1.5)/[Mn] = 0.85 (En la Fórmula 1, [Si], [Al] y [Mn] representan los contenidos (% en peso) de Si, Al y Mn, respectivamente).