IMPROVED 7XXX ALUMINUM ALLOYS

New 7xxx aluminum alloys alloys are disclosed. The new 7xxx aluminum alloys may include 5.0 - 9.0 wt. % Zn, 1.30 - 2.05 wt. % Mg, 1.10 - 2.10 wt. % Cu, wherein 2.55 ⿤ (wt. % Cu + wt. % Mg) ⿤ 3.85, at least one of (i) 0.03 - 0.40 wt. % Mn and 0.02 - 0.15 wt. % Zr, wherein 0.05 ⿤ (wt. % Zr + wt. % Mn) ⿤ 0.50, up to 0.20 wt. % Cr, up to 0.20 wt. % V, up to 0.20 wt. % Fe, up to 0.15 wt. % Si, up to 0.15 wt. % Ti, and up to 75 ppm B, the balance being aluminum, incidental elements and impurities. The new 7xxx aluminum alloys may be in the form of a 7xxx aluminum alloy sheet product having a thickness of from 0.5 to 4.0 mm and comprising at least 15 vol. % recrystallized grains. The new alloys may realize an improved combination of at least two of strength, elongation, fracture behavior and corrosion resistance. Se describen nuevas aleaciones de aluminio 7xxx. Las nueva aleaciones de aluminio 7xxx pueden incluir 5.0 - 9.0 % en peso de Zn, 1.30 - 2.05 % en peso de Mg, 1.10 - 2.10 % en peso de Cu, en donde 2.55 = (peso % Cu + peso % Mg) = 3.85, al menos uno de (i) 0.03 - 0.40 % en peso de Mn, y 0.02 - 0.15 % en peso de Zr, en donde 0.05 = (peso % Zr + peso % Mn) = 0.50, hasta 0.20 % en peso de Cr, hasta 0.20 % en peso de V, hasta 0.20 % en peso de Fe, hasta 0.15 % en peso de Si, hasta 0.15 % en peso de Ti, y hasta 75 ppm B, el resto es aluminio, elementos secundarios e impurezas. Las nuevas aleaciones de aluminio 7xxx pueden tener la forma de un producto tipo lámina de aleación de aluminio 7xxx que tiene un grosor de 0.5 a 4.0 mm y que comprende al menos 15 % en volumen de granos recristalizados. Las nuevas aleaciones pueden conseguir una combinación mejorada de al menos dos de resistencia, elongación, comportamiento de fractura y resistencia a la corrosión.