POLYESTER COMPOSITION FOR EXTRUSION BLOW MOLDED CONTAINERS WITH IMPROVED AGING AND DROP PERFORMANCE

The present invention relates to a polyester resin for extrusion blow molded containers comprising a branched copolymer and fumed silica to improve the aged drop performance said branched copolyester is made from the reaction of purified terephthalic acid or its dimethyl ester, ethylene glycol, bifunctional diacid other than terephthalic acid, diol other than ethylene glycol, and multifunctional compound having a least 3 carboxyl groups, hydroxyl groups and/or ester forming groups thereof, said fumed silica has a particle size of 0.1 to 5 microns and is present at about 100 ppm to about 2,500 ppm based on the weight of said copolyester. La presente invención se relaciona con una resina de poliéster para recipientes moldeados por extrusión y soplado que comprende un copolímero ramificado y sílice pirógena para mejorar el comportamiento de la resistencia a la caída con el envejecimiento, el copoliéster ramificado se elabora con la reacción de ácido tereftálico purificado o su dimetiléster, etilenglicol, diácido bifuncional en lugar de ácido tereftálico, diol en lugar de etilenglicol, y compuesto multifuncional que tiene al menos 3 grupos carboxílicos y/o grupos que forman éster de este, la sílice pirógena tiene un tamaño de partícula de 0.1 a 5 micrómetros y está presente en aproximadamente 100 ppm a alrededor de 2,500 ppm con base en el peso del copoliéster.