SYNTACTIC POLYURETHANE ELASTOMERS HAVING DISTINCT MORPHOLOGY FOR USE IN SUBSEA PIPELINE INSULATION

Syntactic polyurethane elastomers are made using a non-mercury catalyst. The elastomer is made from a reaction mixture containing a polyether polyol, a chain extender, a polyisocyanate and microspheres. The elastomer is characterized morphologically by the presence of small discrete morphological domains 0.1 to 3 μm in diameter, and the substantial absence of discrete morphological domains 5 to 30 μm in diameter. The elastomer adheres well to itself, which makes it very useful as thermal insulation for pipelines and other structures that have a complex geometry. Los elastómeros de poliuretano sintácticos se hacen usando un catalizador sin mercurio. El elastómero está hecho de una mezcla de reacción que contiene un poliéter poliol, un extensor de cadena, un poliisocianato y microesferas. El elastómero se caracteriza morfológicamente por la presencia de pequeños dominios morfológicos discretos de 0.1 a 3 µm de diámetro, y la ausencia considerable de dominios morfológicos discretos de 5 a 30 µm de diámetro. El elastómero se adhiere bien a sí mismo, lo que lo hace muy útil como aislamiento térmico para tuberías y otras estructuras que tienen una geometría compleja.