BWR START UP CORROSION PROTECTION

The oxidizing chemistry environment of BWR reactor water is a key factor promoting intergranular stress corrosion cracking of stainless steel and nickel based alloys used in reactor coolant system piping and vessel internals. This is typically mitigated during power operation with hydrogen injection. However, this method is only effective when the reactors are at power. Accordingly, this invention proposes a method of reducing electrochemical corrosion potential during the start-up phase of BWR reactors. The method includes the steps of providing a mitigation additive adapted to reduce electrochemical corrosion of a BWR reactor; and injecting the mitigation additive into the BWR reactor at a predetermined location prior to hydrogen injection coming online. El ambiente de química oxidante del agua de un reactor de BWR, es un factor clave que promueve el agretamiento intergranular por corrosión bajo tensión de aleaciones basadas en níquel y acero inoxidable, utilizadas en tuberías y componentes internos del sistema refrigerante del reactor. Esto típicamente se mitiga durante operación en régimen de potencia con inyección de hidrógeno. Sin embargo, este método solo es efectivo cuando los reactores están operando. De acuerdo con esto, esta invención propone un método para reducir el potencial de corrosión electroquímica durante la fase de arranque de reactores BWR. El método incluye las etapas de proporcionar un aditivo de mitigación, adaptado para reducir la corrosión electroquímica de un reactor BWR; e inyectar el aditivo de mitigación en el reactor BWR en un sitio predeterminado antes de que la inyección de hidrógeno entre en línea.